Powder composite cement grinding additive and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A composite cement and grinding aid technology, which is applied in cement production, solid waste management, sustainable waste treatment, etc., can solve the problems of harmful chloride ions, low cost, high cost, etc., and achieve increased dosage, increased strength, and improved utilization volume effect
Inactive Publication Date: 2011-04-06
兰州宏方新型建材科技有限公司
View PDF3 Cites 7 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Liquid grinding aids are characterized by convenient storage, transportation and addition, but the disadvantage is that the cost is relatively high
Powder grinding aids are characterized by low cost, but large dosage, and most of them contain chloride ions that endanger the quality of cement
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0019] Embodiment 1 A kind of powder composite cement grinding aid, this grinding aid is made up of the raw material of following mass percent: triethanolamine 4%, sodium tripolyphosphate 10%, nitrate 11%, sodium sulfate 10%, sulfuric acid Calcium 10%, fly ash 55%.
[0020] The preparation method of this grinding aid comprises the following steps:
[0021] (1) Weigh each raw material by proportioning;
[0022] (2) Grinding nitrate, calcium sulfate and fly ash respectively, and passing through a 400×400 mesh sieve to obtain nitrate powder, calcium sulfate powder and fly ash;
[0023] (3) Put nitrate powder and calcium sulfate powder into an airtight mixer for stirring. After mixing evenly, first add sodium tripolyphosphate, sodium sulfate and fly ash powder for stirring until uniform, then add triethanolamine for further mixing. Stir and mix well.
Embodiment 2
[0024] Embodiment 2 A kind of powder composite cement grinding aid, this grinding aid is made up of the raw material of following mass percentage: triethanolamine 5%, sodium tripolyphosphate 6%, nitrate 10%, sodium phosphate 14%, sulfuric acid Calcium 5%, fly ash 60%.
[0025] The preparation method of this grinding aid is with embodiment 1.
Embodiment 3
[0026] Example 3 A powder composite cement grinding aid, the grinding aid is composed of the following raw materials in mass percentages: 10% triethanolamine, 6% sodium tripolyphosphate, 10% salt, 15% sodium sulfate, sulfuric acid Calcium 12%, fly ash 47%.
[0027] The preparation method of this grinding aid is with embodiment 1.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a powder composite cement grinding additive comprising the following raw materials in percentage by weight: 4-10 percent of trolamine, 6-10 percent of trimeric sodium phosphate, 10-15 percent of mirabilite, 10-15 percent of anhydrous sodium sulphate, 5-15 percent of calcium sulphate and 35-65 percent of pulverized fuel ash. By adopting the invention, the addition amount of the grinding additive in the production of each ton of cement can be effectively reduced, the addition amount of mixed material and the utilization amount of the pulverized fuel ash can be effectively improved and the effects for saving energy and reducing consumption can be achieved, thereby the cement strength can be effectively improved, wherein the strength after three days can be improved by 2-3MPa and the strength after 28 days can be improved by 3-6MPa. Meanwhile, the invention also discloses a preparation method of the grinding addictive.
Description
technical field [0001] The invention relates to the field of cement production, in particular to a powder composite cement grinding aid and a preparation method thereof. Background technique [0002] Grinding aids currently on the market are mainly divided into powders and liquids. Liquid grinding aids are characterized by convenient storage, transportation and addition, but the disadvantage is that the cost is relatively high. Powder grinding aids are characterized by low cost, but they are used in large quantities, and most of them contain chloride ions that endanger the quality of cement. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a powder composite cement grinding aid that does not contain chloride ions and effectively improves the utilization of fly ash. [0004] Another technical problem to be solved by the present invention is to provide a preparation method of powder composite cement grinding aid w...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more