Process for welding WQ890D thick plate
A technology of welding process and welding tools, which is applied in the field of WQ890D thick plate welding process, can solve the problems of delaying cold cracks, affecting the production quality and safe operation of large-tonnage crawler cranes, and achieves the effects of eliminating welding cracks, low cost and easy operation
Inactive Publication Date: 2011-06-15
SHANGHAI SANY TECH
View PDF6 Cites 7 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, the welding of high-strength steel materials is prone to delayed cold cracks, which mainly occur at the weld root of circular butt welds and longitudinal welds, T-shaped joints and the connection parts of frame ribs
This has seriously affected the production quality and safe operation of large-tonnage crawler cranes
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| diameter | aaaaa | aaaaa |
| width | aaaaa | aaaaa |
Login to View More
Abstract
The invention provides a process for welding a WQ890D thick plate. In the process, MAG / RK350 or KR500 is used as a welding tool; a backing welding wire is JM-68, a filling welding wire is UnionX90, and the diameters of the backing welding wire and the filling welding wire are both 1.2mm; CO2 is used as protective atmosphere, and the flow velocity of the CO2 gas is 16 to 24L / min; preheating temperature is 100 to 150 DEG C; backing current is 200 to 240 A, voltage is 21 to 29V, multilayer backing is performed, and interpass temperature is 100 to 150 DEG C; filling current is 220 to 270 DEG C, voltage is 24 to 29V, multilayer multi-pass welding is performed, and interpass temperature is 100 to 150 DEG C; and after welding, heat treatment is performed, the heat treatment temperature is 300 to350 DEG C and heat is preserved for 2 hours. In the process for welding the WQ890D thick plate, welding cracks on high-intensity steel materials are effectively eliminated by selecting the optimally matched welding materials and optimum welding process parameters so as to obtain high-quality seams and stable welding structures, and fully meet the requirements of the high-intensity steel during actual use and the welding process is convenient to operate and low in cost.
Description
A WQ890D thick plate welding process technical field The invention relates to a welding process, in particular to a WQ890D thick plate welding process. Background technique With the development of welding structures with high parameters, light weight and large scale, high-efficiency hydraulic transmission and support have been widely used in construction machinery and mining machinery. Correspondingly, it is required to greatly increase the load-carrying capacity of the welded structure under the condition that the self-weight does not increase much. In order to meet the above work requirements, high-strength steel welded structures must be used. In particular, with the continuous development of crawler cranes, especially the rapid development of large-tonnage crawler cranes in recent years, the requirements for the use and welding of high-strength steel materials are getting higher and higher. Specifically, in some large-tonnage crawler cranes, WQ890D high-strength ste...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): B23K31/02
Inventor 付沛邓鉴棋
Owner SHANGHAI SANY TECH