Preparation method of ultra-strong elasticized dual-network winding silk fabric

A screw extruder, polymer technology, applied in the direction of one-component copolyester rayon, filament/thread forming, textile and paper making, etc. Very scratched, feathers are not plump, etc.

Active Publication Date: 2011-12-28
福建百宏聚纤科技实业有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the all-polyester microfiber fabric known as ordinary double-sided coral velvet that is currently seen is made of 150D / 288F or 75D / 144F or 100D / 144F DTY as the suede surface, so the weight is generally 280- 350g / m 2 Between 4-5.5mm, the pile height is about 4-5.5mm, which is restricted by the gram weight and pile height, so this kind of fabric shows the following two deficiencies, one is that the suede is thin, and it shows a thin flat effect when stretched; the other is After fluffing on the reverse side, obvious unevenness will be left on the surface (front side), resulting in poor three-dimensional effect, less plump down feathers, and weak hand feeling
This kind of fabric is not super elastic enough. At the same time, because it cannot form a double network of network yarn, it cannot show the fluffy, soft, smooth and scratchy, plump and skinny style compared with acrylic plush fabric.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] A method for preparing a super-strength elastic double network yarn fabric made of polymer heated by a low-temperature screw extruder, comprising three process steps of elastic double network yarn manufacturing, knitting and weaving, and dyeing and finishing, and is characterized in that:

[0011] 1. The manufacturing process of stretched double network yarn: the raw material is a homogeneous mixture of high crystalline polymer of ethylene terephthalate copolyester and high crystalline polymer of polytrimethylene terephthalate, using sulfamic acid Combination of two substances with alumina as a catalyst, the above mixture is first formed into a prepolymer, and then the prepolymer is subjected to a polycondensation reaction under high temperature and vacuum conditions to form a low-viscosity polymer, which is fed into a screw extruder, where the screw The heating temperature from the feed section to the discharge section of the extruder is in the low temperature range of ...

Embodiment 2

[0014] A method for preparing a super-strength elastic double network yarn fabric made of polymer heated by a low-temperature screw extruder, comprising three process steps of elastic double network yarn manufacturing, knitting and weaving, and dyeing and finishing, and is characterized in that:

[0015] 1. The manufacturing process of stretched double network yarn: the raw material is a homogeneous mixture of high crystalline polymer of ethylene terephthalate copolyester and high crystalline polymer of polytrimethylene terephthalate, using sulfamic acid Combination of two substances with alumina as a catalyst, the above mixture is first formed into a prepolymer, and then the prepolymer is subjected to a polycondensation reaction under high temperature and vacuum conditions to form a low-viscosity polymer, which is fed into a screw extruder, where the screw The heating temperature from the feed section to the discharge section of the extruder is in the low temperature range of ...

Embodiment 3

[0018] A method for preparing a super-strength elastic double network yarn fabric made of polymer heated by a low-temperature screw extruder, comprising three process steps of elastic double network yarn manufacturing, knitting and weaving, and dyeing and finishing, and is characterized in that:

[0019]1. The manufacturing process of stretched double network yarn: the raw material is a homogeneous mixture of high crystalline polymer of ethylene terephthalate copolyester and high crystalline polymer of polytrimethylene terephthalate, using sulfamic acid Combination of two substances with alumina as a catalyst, the above mixture is first formed into a prepolymer, and then the prepolymer is subjected to a polycondensation reaction under high temperature and vacuum conditions to form a low-viscosity polymer, which is fed into a screw extruder, where the screw The heating temperature from the feed section to the discharge section of the extruder is in the low temperature range of 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of ultra-strong elasticized dual-network winding silk fabric made from polymer and heated by low temperature screw extruder, which comprises three process steps, namely manufacturing of elasticized dual-network winding silk, knitting and weaving, and dyeing and finishing, and the ultra-strong elasticized dual-network winding silk fabric which has excellent fluffy, soft, smooth, straight, plump and skinny style incomparison with acrylic fiber plush fabric by improving and optimizing related processes and parameters in the steps.

Description

technical field [0001] The invention relates to a preparation method of a super-strength elastic double network silk fabric made of polymer heated by a low-temperature screw extruder. Background technique [0002] The steps included in the preparation method of stretched double network silk fabric are well known in the industry by taking the processing of warp knitting machine as an example. The specific steps are: DTY silk material selection (raw material preparation), warping, weaving, slitting, dyeing Or printing, loose drying, color fixing, finishing, heat setting, back raising finishing, sewing, and finishing into fabrics. In view of the fact that all polyester (also known as pure polyester) microfiber has a texture like cotton wool, it is widely used to process clothing, toys, shoes, hats, composite floor mats, quilted mats, bedding, etc.; and in view of pure polyester Microfiber fabric has good warmth retention. Therefore, in recent years, it has gradually replaced...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01D5/22D01D5/253D01D5/088D04B1/20D01F6/84D06M11/76D06M13/188D06P3/52D06M101/32
Inventor 叶敬平