Novel sole production method

A production method and new technology, applied in footwear, other household appliances, household appliances, etc., can solve the problems of labor, the forefoot cannot be bent, and the process is complicated, and achieve the effect of maintaining physical and mechanical properties and saving mold costs.

Inactive Publication Date: 2011-09-07
佛山市南海建诺鞋业有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, since the hardness of the entire sole is very hard, the hardness of the forefoot will make it impossible to bend at this time, making it extremely difficult for people to walk, and the feet are easily fatigued.
In addition, in some advanced production processes, a soft inner pad or other similar material will be placed on the hard bottom platform or midsole of the forefoot, but it cannot change the current situation of bending the soles of the feet when walking, and it will still be very tiring; , and some processes are a combination of two products through heel hardening and forefoot softening, but the process is complicated and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel sole production method
  • Novel sole production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] Such as figure 1 Shown, the production method of novel sole described in the embodiment of the present invention, its main steps comprise:

[0017] (1) The injection material is divided into two parts. Firstly, the raw materials of the rear part hard material 1 and the front part soft material 2 are respectively prepared, and the rear part hard material 1 is composed of mixed isocyanate, mixed polyol and additional materials. Composition, the additional material includes amine catalyst, metal amine catalyst, ethylene glycol, talcum powder, foaming agent, color paste, if the latter part of the hard material 1 is a total of 100 parts of all raw materials, then the above additional materials (except color paste) The mass fraction can be 1-1.2%, 0.3-0.5%, 5-6%, 8-10%, 1-1.2% in turn; the front part of the soft material 2 is composed of isocyanate, polyol and additional materials. The additional material includes amine, ethylene glycol, foaming agent, and color paste. If th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a novel sole production method, which mainly comprises the following steps of: respectively preparing a rear part hard material and a front part soft material, wherein the rear part hard material consists of mixed isocyanate, mixed polyalcohol and additives, and the additives comprise an amine catalyst, a metal amine catalyst, glycol, talcpowder, a foaming agent and color cream; regulating reaction time of the hard material to be about 15 seconds, and curing within 3-5 minutes; and lifting the front tip of a die body 45 degrees relative to the ground, injecting the hard material for about 10-12 seconds, injecting the soft material, performing die assembly for 6 to 7 minutes, and demoulding. The novel sole production method has the advantages that: two types of soles with different hardness are manufactured in a once molding mode, the problem of electricity, labor and time cost due to post forming required by common dual density is solved, the problem that several dual density production processes cannot be used structurally is solved, and the mold cost is greatly saved.

Description

technical field [0001] The invention relates to a material injection process for shoe soles, in particular to a production method for a novel shoe sole. Background technique [0002] When producing polyurethane women's high-heeled outsoles by traditional methods, it is usually necessary to ensure the stiffness of the high-heel so as not to twist the foot when wearing it. Therefore, since the hardness of the entire sole is very hard, the hardness of the forefoot at this time will make it impossible to bend, making it extremely strenuous for people to walk, and the feet are prone to fatigue. In addition, in some advanced production processes, a soft inner pad or other similar material will be placed on the hard bottom platform or midsole of the forefoot, but it cannot change the current situation of bending the soles of the feet when walking, and it will still be very tiring; , and some processes are a combination of two products through heel hardening and forefoot softening,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B29D35/12B29C45/16
Inventor 许建华
Owner 佛山市南海建诺鞋业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka