High elastic non-ironing cellulose fiber and preparation method thereof

A technology of cellulose fiber and cellulose, applied in the field of cellulose fiber and its preparation, to achieve the effects of saving cost and energy, good wrinkle resistance, and excellent mechanical properties

Active Publication Date: 2013-02-27
QINGDAO TIANYI GROUP
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

So far, research in this area has not been reported

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High elastic non-ironing cellulose fiber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] A preparation method of highly elastic non-ironing cellulose fibers, the preparation method comprising the steps of:

[0037] a. Vacuum-dry the selected cellulose at 60-100°C for 2-5 hours for later use. The cellulose can be one of cotton pulp cellulose, wood pulp cellulose or bamboo pulp cellulose;

[0038] b Weigh the finishing agent according to 6.6% to 11.6% of the mass of the selected cellulose, weigh the catalyst according to 3.3% to 5.8% of the mass of the selected cellulose, and weigh the ionic liquid according to 10 to 50 times the mass of the selected cellulose, Then, mix the weighed finishing agent, catalyst and ionic liquid, heat to 30° C. to 40° C., stir to dissolve, and obtain a modified solution. The finishing agent can be one of 1,2,3,4-cyclopentadinic acid or citric acid or 1,2,3,4-butane tetracarboxylic acid, and the catalyst can be sodium hypophosphite or sodium phosphite or sodium nitrate, and the ionic liquid can be 1-allyl-3-methylimidazole acetat...

Embodiment 1

[0047] Vacuum dry the cotton pulp cellulose at 100°C for 2 hours, weigh 20g for later use; add 2.32g of 1,2,3,4-cyclopentadinic acid and 1.16g of sodium hypophosphite to 1000g of 1-allyl-3 - Methylimidazolium acetate ionic liquid, the solution is heated to 30°C, then stirred to dissolve to obtain a modified solution; 20g of spare dry cotton pulp cellulose is added to the above modified solution, and the solution is heated to 80°C , then stirred to dissolve it, and then degassed under reduced pressure for 20 hours to obtain a modified spinning solution; prepare a sulfuric acid solution with a mass percentage concentration of 1%, and heat it to 50°C for later use; the modified spinning solution is sprayed under pressure into the acid solution prepared above, solidified for 30s, and then stretched in three stages, each stretching ratio was 1.5 times, to obtain shaped fibers; put the shaped fibers into an oven, pre-baked at 80°C for 5min, and then 160°C ℃ for 2 minutes; the baked ...

Embodiment 2

[0049] The wood pulp cellulose was vacuum-dried at 60°C for 5 hours, and 100 g was weighed for later use; 6.6 g of citric acid and 3.3 g of sodium phosphite were sequentially added to 1000 g of 1-allyl-3-methylimidazolium chloride salt ionic liquid, The solution was heated to 40°C, and then stirred to dissolve it to obtain a modified solution; 100g of spare dry wood pulp cellulose was added to the above modified solution, the solution was heated to 80°C, stirred again to dissolve it, and then decompressed to remove Soak for 20 hours to obtain a modified spinning solution; prepare a phosphoric acid solution with a mass percentage concentration of 3%, and heat it to 30°C for use; under pressure, the modified spinning solution passes through the spinneret and enters the above-mentioned prepared acid solution , solidified for 30s, and then carried out three stages of drawing, and the drafting ratio of each stage was 2.0 times to obtain shaped fibers; put the shaped fibers into an o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high elastic non-ironing cellulose fiber and a preparation method thereof, and belongs to the technical field of weaving. The high elastic non-ironing cellulose fiber is prepared from cellulose, a finishing agent and a catalyst through a cross linking reaction, and comprises, by mass, 85%-91% of the cellulose, 6%-10% of the finishing agent and 3%-5% of the catalyst. The high elastic non-ironing cellulose fiber provided by the present invention has advantages of excellent mechanical property, natural tactility, comfortable elasticity and good wrinkle resistance, can suffer a plurality of slashing washing technologies and finishing technologies, and can be widely applicable for products such as non-ironing shirts, trousers and suits so as to satisfy consumer demands of easy-care clothing and easy-care fabric. Due to the fiber with high elasticity, textile produced from the fiber provided by the present invention has excellent wrinkle resistance without ironing and finishing. With the present invention, processing enterprises of fabric and clothing can save cost and energy.

Description

technical field [0001] The invention relates to a cellulose fiber with high elasticity and non-ironing performance and a preparation method thereof, belonging to the field of textile technology production and processing. Background technique [0002] With the progress of society, the development of science and technology and the improvement of living standards, people's clothing consumption concept and market demand have undergone significant changes. The requirements for fibers and textiles are not only durable and beautiful, but also the pursuit of textiles. Wearing comfort, health, safety protection and environmental protection. Cellulose fiber is made from natural materials and has excellent properties such as good hygroscopicity, strong air permeability, comfortable wearing, easy dyeing, and natural environmental protection. It meets people's requirements for comfort, environmental protection and health, and is favored by consumers. However, the wrinkle resistance of c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F2/28C08B3/12
Inventor 朱平张传杰张建伟王柳
Owner QINGDAO TIANYI GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap