Honeycomb aluminium foil material
A technology of aluminum foil and honeycomb, which is applied in the field of honeycomb aluminum foil materials, can solve the problems of the aluminum honeycomb foil material being unqualified, the performance gap of the aluminum honeycomb foil, and the inability to meet the market demand, etc., and achieve the effects of stable product quality, increased strength, and improved plasticity
Inactive Publication Date: 2011-10-05
DENGFENG YINHE ALUMINUM FOIL
View PDF5 Cites 2 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, due to the unstable technology of some domestic aluminum processing enterprises, mainly the materials of aluminum honeycomb foil are not up to standard, resulting in a gap between the performance of domestic aluminum honeycomb foil and foreign countries, which cannot meet market demand
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0015] Honeycomb aluminum foil material, its composition and weight percentage are: Cu: 0.03%; Fe: 0.6%; Mn: 1.0%; Si: 0.3%; Mg: 0.08%; Re: 0.6%; the balance is Al.
Embodiment 2
[0017] Honeycomb aluminum foil material, its composition and weight percentage are: Cu: 0.06%; Fe: 0.3%; Mn: 0.8%; Si: 0.2%; Mg: 0.05%; Re: 0.4%; the balance is Al.
Embodiment 3
[0019] Honeycomb aluminum foil material, its composition and weight percentage are: Cu: 0.01; Fe: 0.2%; Mn: 0.5%; Si: 0.1%; Mg: 0.02%; Re: 0.2%; the balance is Al.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses a honeycomb aluminium foil material which comprises the following components by weight: 0.01-0.1% of Cu; 0.2-0.9% of Fe; 0.5-1.5% of Mn; 0.1-0.4% of Si; 0.02-0.1% of Mg; 0.2-0.8% of Re; and the balance of Al. According to the invention, aluminium foil components used for aluminium honeycomb cores are optimized, which effectively increases mechanical properties of the aluminium foil, increases plasticity and processing performance of the aluminium foil, and improves product quality.
Description
technical field [0001] The invention relates to the aluminum processing industry, in particular to a honeycomb aluminum foil material. Background technique [0002] Aluminum honeycomb foil is the main material for making aluminum honeycomb panels. Aluminum honeycomb panels are widely used in construction, transportation, electronics and other fields due to their excellent properties such as high wind pressure resistance, shock absorption, sound insulation, heat preservation, flame retardancy and high specific strength. At the same time, the application of aluminum honeycomb panels in high-performance and lightweight fields such as high-speed trains, aircraft and aerospace, as well as in low-cost, modern furniture industries with strict environmental protection requirements is gradually expanding. The aluminum honeycomb core plays a supporting role in the honeycomb panel, and the strength of the aluminum honeycomb core directly affects the performance of the aluminum honeyco...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More IPC IPC(8): C22C21/00
Inventor 韩跃继贾丙年张建敏
Owner DENGFENG YINHE ALUMINUM FOIL