Method for improving magnetic properties of cold rolling non-oriented silicon steel
A technology of oriented silicon steel and magnetism, which is applied in the production field of cold-rolled non-absorbing silicon steel, can solve problems such as different control parameters, magnetic deterioration, and inability to decarburize, and achieve low cost of coating liquid, large magnetic amplitude, and reduced internal oxidation.
Inactive Publication Date: 2013-10-16
北京中钢贸科技发展有限公司
View PDF5 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
These controls are very complicated, and the control parameters are different for different original carbon contents, different silicon contents, different thicknesses, and different speeds.
If the control is not accurate, there will be no carbon decarburization, or surface oxidation hinders decarburization, and even internal oxidation will cause magnetic deterioration
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0027] Now in conjunction with the examples, the finished product free silicon steel of the present invention is further described.
[0028] Such as figure 1 Shown, the present invention improves the method for cold-rolled non-oriented silicon steel magnetism, and the method steps are as follows: pickling, cold rolling, continuous annealing, in described continuous annealing step, also have the following steps:
[0029] a. Add a set of inorganic salt coating device in the continuous annealing and cleaning system, and the silicon steel strip after cold rolling is evenly coated with a layer of inorganic salt solution by the inorganic salt coating device;
[0030] B, the weight percentage of described inorganic salt solution is: K 2 CO 3 0.5~5.0%, NaCl 0.5~2%, MgO 1~8%, the rest is H 2 O; For different numerical selections, the experimental results are shown in Table 1:
[0031] Table I
[0032]
[0033] c, the coating quantity of described inorganic salt solution i...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses a method for improving the magnetic properties of cold rolling non-oriented silicon steel, which comprises the following steps of : acid-washing, cold rolling and continuously annealing; the step continuously annealing: adding an inorganic salt coating device in a continuous annealing and washing system, and uniformly coating a layer of inorganic salt solution on a cold-rolled silicon steel strip through the inorganic salt coating device, wherein the inorganic salt solution contains the following components in weight percentage: 0.5-5.0% of K2CO3, l0.5-2% of NaC10, 1-8% of MgO and the rest of H2O, the coating quantity of the inorganic salt solution is 1-50gm<3>, the plate passing speed is 5-400m / min, and the coated silicon steel strip is dried in a hot air drier, and then, a layer of brown-back fayalite film is formed on the surface of the coated silicon steel strip; and carrying out degradation and decarburization to the silicon steel. In the invention, after the cold-rolled silicon steel is coated with the inorganic salt to form the brown-back fayalite film, so that the decarburization effect is improved, the internal oxidation of the silicon strip can be reduced, and the magnetic properties of the silicon steel strip finished product can be stably improved.
Description
technical field [0001] The invention relates to the production of cold-rolled silicon-free steel. Background technique [0002] like figure 1 As shown, it is part of the production process of cold rolling. Cold rolled silicon steel is a handicraft in steel, and is also a technical product with high added value, high technology content, complex production process, and long process cycle, which usually includes pickling (normalization), Primary cold rolling, intermediate annealing, secondary cold rolling, continuous decarburization annealing coating insulation layer (cycle) and shear packaging and other methods. For non-oriented silicon steel, the main method to determine the magnetic properties of the finished non-oriented silicon steel is continuous decarburization annealing and insulating layer coating. The purpose of this process is as follows. [0003] (1) Complete recrystallization and grow the grains, and finally form perfect and uniform recrystallization grains to ob...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): C21D8/12C21D1/68
Inventor 王永颜华魏庆媛
Owner 北京中钢贸科技发展有限公司