Liquid photosensitive solder resist white oil and manufacturing method thereof

A technology of photosensitive solder resist and manufacturing method, applied in optics, ink, opto-mechanical equipment, etc., can solve the problems of discoloration, yellowing of solder resist white oil, etc. Effect

Active Publication Date: 2012-02-15
江门市阪桥电子材料有限公司
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a liquid photosensitive solder resist white oil and its production method, which solves the problems of the existing traditional solder resist white oil turning yellow after high temperature, serious discoloration, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Liquid photosensitive solder resist white oil and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The preparation method of the liquid photosensitive solder resist white oil is as follows: mix 40 g of the main agent and 10 g of the curing agent, stir evenly, and then irradiate active energy rays until the Stuffer series reaches 9.

Embodiment 2

[0041] The preparation method of the liquid photosensitive solder resist white oil is as follows: mix 40 g of the main agent and 10 g of the curing agent, stir evenly, and then irradiate active energy rays until the Stuffel series reaches 11.

Embodiment 3

[0043] The preparation method of the liquid photosensitive solder resist white oil is as follows: mix 40 g of the main agent and 10 g of the curing agent, stir evenly, and then irradiate active energy rays until the Stuffel series reaches 12.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses liquid photosensitive solder resist white oil and a manufacturing method thereof. The liquid photosensitive solder resist white oil is prepared from a main agent and a curing agent according to a mass ratio of 4: 1. The manufacturing method of the liquid photosensitive solder resist white oil comprises the following steps of mixing the main agent and the curing agent according to a mass ratio of 4: 1, stirring uniformly, carrying out silkscreen of the mixture on a printed circuit board (PCB), carrying out prebaking, and carrying out irradiation by active energy rays until a Stouffer level reaches a level of 9 to 12. The liquid photosensitive solder resist white oil has excellent photonasty (light sensitivity) and can be cured rapidly. The liquid photosensitive solder resist white oil can be developed by a dilute alkali solution and form patterns, and can form a cured film by thermocuring in a post-curing process, wherein the cured film has good adhesiveness and high-temperature resistance.

Description

technical field [0001] The invention relates to a liquid photosensitive solder resist white oil used for manufacturing precision circuit boards and emerging LEDs and a preparation method thereof. Background technique [0002] Similar products are easy to change color after high temperature immersion tin, are not resistant to high temperature, and have serious yellowing after reflow soldering. Contents of the invention [0003] The object of the present invention is to provide a liquid photosensitive solder resist white oil and its preparation method, which solves the problems of the existing traditional solder resist white oil turning yellow after high temperature, serious discoloration and the like. [0004] In order to achieve the above-mentioned design purpose, the technical scheme adopted in the present invention is as follows: [0005] A liquid photosensitive solder resist white oil is mainly composed of a main agent and a curing agent in a mass ratio of 4:1. [000...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D11/10G03F7/004G03F7/027C09D11/101
Inventor 李铨华
Owner 江门市阪桥电子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com