Special printing glaze material for ceramic full-polished glaze
A technology of full glaze polishing and printing glaze, applied in the field of glaze, can solve the problem of unmaintainable gloss, and achieve the effect of cost reduction, quality improvement and competitiveness improvement.
Inactive Publication Date: 2012-07-04
CARLOBBIA GLAZE KUNSHAN
View PDF0 Cites 2 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, due to the lack of existing glaze technology, after the general ceramic metal is polished, the glossiness of the metallic texture of the ceramic metal glaze layer, the test of dirt absorption, the surface hardness and the shape of the tile can not be maintained. in standard data
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0016] When the firing temperature of a firing ceramic tile is about 1190-1220°C, the special printing glaze for ceramic tile of the present invention, calculated by weight percentage, contains the following components: 1004 15 ﹪
[0017] 2006 2 ﹪
[0018] 2008 3 ﹪
[0019] Frit 80%.
Embodiment 2
[0021] When the firing temperature of the one-time firing ceramic tile is about 1175-1190℃, another special printing glaze for the ceramic tile of the present invention, calculated by weight percentage, contains the following composition: 1004 13 ﹪
[0022] 2006 1.6 ﹪
[0023] 2008 2.4 ﹪
[0024] Frit 83%.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention provides a special printing glaze material for ceramic full-polished glaze, which comprises 1004, 2006, 2008 and FKK-7005 clinker. In percentage by mass, the ratio of the 1004 to the 2006 to the 2008 to the FKK-7005 clinker is 15:2:3:80. A full-polished glaze ceramic tile product processed by using the special printing glaze material has good quality indexes such as glaze texture, gloss, transparency, hardness and the like. Different proportions of FKK-7005 clinker can be added according to different firing conditions so as to achieve the effects required by the products. The special printing glaze material for the ceramic full-polished glaze is widely applied to the ceramic full-polished glaze products.
Description
technical field [0001] The invention relates to the technical field of glazes, in particular to a special printing glaze for ceramic tiles. [0002] Background technique [0003] It has largely made ceramic tile products replace the demand for traditional stone materials in the building materials industry, which is in line with the call of the national policy "energy saving and emission reduction". However, due to the lack of existing glaze technology, after the general ceramic metal is polished, the glossiness of the metallic texture of the ceramic metal glaze layer, the test of dirt absorption, the surface hardness and the shape of the tile can not be maintained. in standard data. Contents of the invention [0004] The invention overcomes the shortcomings of the existing glaze technology and provides a special printing glaze for ceramic tiles, which can replace traditional natural stone building materials and increase the direct sales value of products. [0005] The p...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More IPC IPC(8): C04B41/86
Inventor 赵白弟
Owner CARLOBBIA GLAZE KUNSHAN
Features
- R&D
- Intellectual Property
- Life Sciences
- Materials
- Tech Scout
Why Patsnap Eureka
- Unparalleled Data Quality
- Higher Quality Content
- 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com