Method for treating collagen fiber non-woven substrate surface
A substrate surface, collagen fiber technology, applied in the direction of fabric surface trimming, fabric rubbing/softening, textiles and papermaking, etc. problem, to achieve the effect of low cost and simple process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0016] Follow the steps below to surface-treat the collagen fiber nonwoven substrate:
[0017] (1) First, use 180# sandpaper for rough grinding once, and then use 300# sandpaper for fine grinding once, until the surface fluff is soft and fine, and the hand is not rough.
[0018] (2) Grain-like surface layer: Spread the raw material of the grain-like surface layer evenly on the surface of the substrate with a roller coater, apply 3.8g / sf with a scraping roller for the first time, and then roll for a second time after drying. , apply 15g / sf with a No. 17 roller. The raw materials of the grain-like layer are mixed by the following raw materials in mass ratio: leather resin: pigment paste = 250:30.
[0019] (3) Water spray: lightly spray the mixture of nitrocellulose and water on the surface, and the mass ratio of nitrocellulose and water is 60:100.
[0020] (4) Making leather texture: using a roller press under the conditions of temperature 130°C, pressure 130Mpa and 4.5m / min. ...
Embodiment 2
[0027] (1) First, use 180# sandpaper for rough grinding once, and then use 300# sandpaper for fine grinding once, until the surface fluff is soft and fine, and the hand is not rough.
[0028] (2) Grain-like surface layer: Spread the raw material of the grain-like surface layer evenly on the surface of the substrate with a roller coater, apply 4.8g / sf with a scraping roller for the first time, and then roll for a second time after drying. , apply 16g / sf with a No. 17 roller. The raw materials of the grain-like layer are mixed with the following raw materials in mass ratio: leather resin: pigment paste: water = 200:20:5.
[0029] (3) Water spray: lightly spray the mixture of nitrocellulose and water on the surface, and the mass ratio of nitrocellulose and water is 100:150.
[0030] (4) Making leather texture: using a roller press under the conditions of a temperature of 140° C., a pressure of 150 Mpa and a pressure of 5.0 m / min. The pattern is required to be clear, and the pat...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com