Mixed fabric by polyester fiber, cationic polyester fiber and wood pulp fiber

A cationic fiber and wood pulp fiber technology, applied in the field of fabrics and textile fabrics, can solve the problems of alkali resistance but not acid resistance, blurred patterns in subtle areas, and distortion of patterns, and achieve bright colors, strong three-dimensional effects, and realistic patterns. Effect

Inactive Publication Date: 2013-01-30
李国平
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because burnt-out fabrics use the principle of cotton fibers to be alkali-resistant and not acid-resistant, polyester-cotton core-spun yarns are used to weave fabrics, and then through post-processing technology, strong acid is used to corrode the outer cotton yarns to expose the thinner polyester core threads, forming semi-woven fabrics. For transparent patterns, the subtleties of the pattern are often blurred, which makes the pattern distorted

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mixed fabric by polyester fiber, cationic polyester fiber and wood pulp fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] see figure 1 , the present invention relates to a fabric interwoven with polyester fibers, polyester cationic fibers and wood pulp fibers, comprising a burnt-out fabric body 1, the burnt-out fabric body 1 is formed by interweaving warp threads and weft threads, the warp threads are polyester fibers, and the weft threads are wood pulp Fiber mixed with polyester cationic fiber. There is an embroidery layer 2 on the surface of the burnt-out fabric body 1 . The embroidery layer 2 is a layer embroidered on the surface of the burnt-out fabric body 1 with colored threads, and is used to outline the subtleties of the pattern shown by the burn-in fabric body 1 to make the pattern more realistic.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a mixed fabric of polyester fiber, cationic polyester fiber and wood pulp fiber. The burnt-out embroidery fabric includes a burnt-out fabric body (1). The burnt-out fabric body (1) is interwoven by warps and wefts, wherein the warps are polyester fiber, and the wefts are mixed fiber of wood pulp fiber and cationic polyester fiber. An embroidery layer (2) is locally arranged on the surface of the burnt-out fabric body (1). After the embroidery processing to the burnt-out fabric, patterns are more realistic to express the elegance of the burnt-out embroidery fabric. And the fabric is bright in colors, good in air and moisture permeability, fine in touch feeling, and strong in three-dimensional effect; and with a price lower than the price of real silk, the fabric of the invention is suitable for promotion in the home textile market.

Description

(1) Technical field [0001] The invention relates to a fabric, in particular to a fabric for making napkins, curtains and bedspread decorative fabrics, which belongs to the field of textile fabrics. (2) Background technology [0002] Burnt-out fabric refers to the light and thin blended fabric with translucent flower-shaped pattern on the surface. It has good air permeability, strong scratch resistance, quick drying and no ironing. It is the best choice for napkins, curtains, and bedspread decorative fabrics. However, because burnt-out fabrics use the principle that cotton fibers are alkali-resistant and not acid-resistant, polyester-cotton core-spun yarns are used to weave fabrics, and then through post-processing technology, strong acid is used to corrode the outer cotton yarns to expose thinner polyester core threads, forming semi-woven fabrics. For transparent patterns, the subtleties of the pattern are often blurred, resulting in distortion of the pattern. (3) Contents...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06Q1/00D02G3/04D05C17/00
Inventor 李国平
Owner 李国平
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com