Vitrification ceramic tile, preform body of the vitrification ceramic tile and preparation method of vitrification ceramic tile

Abstract

The invention relates to a preform body of a vitrification ceramic tile. A content of Na2O in the preform body is smaller than or equal to 4.53wt%, and a content of K2O is smaller than or equal to 3.66wt%. The preform body of the vitrification ceramic tile limits potassium and sodium contents, overcomes a shortcoming of high brittleness caused by redundancy glass phases in the vitrification ceramic tile, achieves synergistic interaction effects through matching of each component in the vitrification ceramic tile, reduces firing temperature, shortens firing periods and guarantees that products have good process performance and physical and chemical performance.

Description

technical field [0001] The invention relates to a vitrified ceramic brick, a blank thereof and a preparation method thereof, in particular to an ultra-low temperature energy-saving vitrified ceramic brick, a blank thereof and a preparation method thereof, belonging to the field of ceramic processing. Background technique [0002] Vitrified ceramic tiles are one of the main products of architectural ceramics. Its conventional firing temperature is between 1210±20°C, the conventional firing cycle is between 60±5min, and the thickness of conventional products is between 12±2mm. The crystal structure is generally feldspar-mullite structure, and at the same time, a large number of Guangdong black mud and feldspar raw materials, which are relatively scarce in resources, are used in the preparation of vitrified ceramic tiles in the prior art, resulting in a shortage of raw materials for production. Therefore, the existing technology of vitrified ceramic tiles has the problems of th...

AI Technical Summary

Problems solved by technology

[0013] (1) In order to reduce the firing temperature, the amount of clay raw materials added to the ceramic formula is small, so that the strength of the green body is not enough, and it is easy to break when going on the drying line and decoration line;

[0014] (2) In order to reduce the firing temperature and shorten the firing cycle, a large amount of flux raw materials are introduced into the formula, so that the product is prone to wave deformation, size and other defects during firing, which may cause kiln jam accidents in severe cases;

[0015] (3) Introduce a large amount of flux raw materials, so that the strength of the low-viscosity glass phase in the product is low, and it is easy to crack due to the internal stress during firing and cooling;

[0016] (4) T