Abstract

The invention discloses a light and color glazed tile for a building, which is obtained by the following steps: adding 0.4 to 0.6 kg of magnesium oxide to each kilo of a magnesium chloride solution; agitating the mixture for 6 to 8 minutes; successively adding 0.05 to 0.1 kg of magnesium silicate, 0.02 to 0.03 kg of urea-formaldehyde resin, 0.06 to 0.1 g of ammonium carbonate, 2 to 3 g of trisodium phosphate and 2 to 3 g of pigment; agitating the obtained mixture for 20 to 30 minutes; pouring the agitated mixture to a glass fiber cloth; scraping and compacting the poured mixture; and performing natural cure and drying to obtain the light and color glazed tile for the building. In the way above, the light and color glazed tile for the building has the advantages of smooth and clean surface, bright color, color retention, fracture resistance, compression resistance, thermal and cooling shock resistance, acid and alkali resistance, freezing resistance, light weight, low water absorption, good thermal insulation, good sound insulation and low cost.

Description

technical field [0001] The invention relates to the technical field of architectural decoration, in particular to a lightweight colored glazed tile for architectural use. Background technique [0002] With the continuous development of my country's economy in recent years, it has promoted the development of the construction industry. With the continuous development of the current tourism industry, antique architecture is the main measure in the current tourism economic development process, and the national style antique architectural system is also constantly developing, and architectural functions and architectural structures are also constantly changing. [0003] Glazed tiles have been used as traditional Chinese building components because of their solid materials, bright colors, and smooth glaze. After successive developments and quality improvements, glazed tiles have been widely used in modern architecture due to their various excellent functions. [0004] Existing gl...

AI Technical Summary

Problems solved by technology

[0004] Existing glazed tiles are usually fired with a mixture of various mud materials. The glaze layer is generally thick and produces stress. The quality is heavy, and it is easy to cause cracks and cracks on the glazed surface of the product.

Not smooth enough, and the mud is prone to pollution in the production process, high cost and energy consumption, the quality of the product is not stable enough, the gloss of the glaze is not enough, and the color is not rich and stable enough. Fades easily in sunlight