Light anti-slipping high-wear-resistance rubber material for sole and preparation method thereof

A rubber material, high wear-resistant technology, applied in the field of rubber composite materials, can solve the problems of inability to meet strenuous exercise, poor shock absorption, heavy quality, etc.

Active Publication Date: 2013-03-27
MAOTAI FUJIAN SOLES CO LTD
View PDF6 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ordinary rubber soles have the advantages of wear resistance, non-slip, elasticity, and waterproof, but they have the disadvantages of heavy weight, non-slip performance that cannot meet high requirements, and poor shock absorption, which cannot meet the needs of strenuous exercise.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Light anti-slipping high-wear-resistance rubber material for sole and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] The formula of this embodiment is as follows (note: each raw material is by weight)

[0045] EVA: 65

[0046] NR: 15

[0047] SBR: 15

[0048] CaCO3:4

[0049] Si-69 wear agent: 4

[0050] ZnO: 3

[0051] ZnST: 3

[0052] ST: 1.5

[0053] DCP: 1

[0054] AC: 1.8.

[0055] The preparation method is as follows:

[0056] First mix other raw materials except DCP and AC for banburying, add DCP and AC 5 minutes before the end of banburying, granulate after the end of banburying, and then one-time injection molding to obtain the light weight non-slip and high wear-resistant rubber Material.

[0057] During banburying, control temperature is 125 ℃, banburying time is 18min.

[0058] During one injection molding, the control temperature is 185°C and the time is 4min.

Embodiment 2

[0060] The formula of this embodiment is as follows (note: each raw material is by weight):

[0061] EVA: 60

[0062] NR: 10

[0063] SBR: 20

[0064] CaCO3:5

[0065] AG-209 wear agent: 3

[0066] ZnO: 2

[0067] ZnST: 4

[0068] ST: 2

[0069] DCP: 0.8

[0070] AC: 1.5.

[0071] The preparation method is as follows:

[0072] First mix other raw materials except DCP and AC for banburying, add DCP and AC 4 minutes before the end of banburying, granulate after the end of banburying, and then make the above-mentioned light weight non-slip and high wear-resistant rubber by one injection molding Material.

[0073] During banburying, control temperature is 120 ℃, banburying time is 20min.

[0074] During one injection molding, the temperature is controlled at 180°C and the time is 5 minutes.

Embodiment 3

[0076] The formula of this embodiment is as follows (note: each raw material is by weight):

[0077] EVA: 70

[0078] NR: 20

[0079] SBR: 10

[0080] CaCO3:3

[0081] Si-69 wear agent: 5

[0082] ZnO: 4

[0083] ZnST: 2

[0084] ST: 1

[0085] DCP: 1.2

[0086] AC: 2.

[0087] The preparation method is as follows:

[0088] First mix other raw materials except DCP and AC for banburying, add DCP and AC 6 minutes before the end of banburying, granulate after banburying, and then make the above-mentioned light weight non-slip and high wear-resistant rubber by one injection molding Material.

[0089] During banburying, control temperature is 135 ℃, banburying time is 12min.

[0090] During one-time injection molding, the temperature is controlled at 195°C and the time is 3 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a rubber composite material and particularly relates to a light anti-slipping high-wear-resistance rubber material for a sole and a preparation method thereof. The light anti-slipping high-wear-resistance rubber material for the sole is prepared from the following raw materials in parts by weight: 55-75 parts of EVA (Ethylene Vinyl Acetate), 8-25 parts of NR (Natural Rubber), 8-25 parts of SBR (Styrene Butadiene Rubber), 2-6 parts of CaCO3, 2-6 parts of wear-resisting agent, 1-5 parts of ZnO, 1-5 parts of ZnST, 0.5-2.5 parts of ST, 0.5-1.5 parts of DCP (Dibasic Calcium Phosphate) and 1.2-2.5 parts of AC (Azodicarbonamide). Compared with the prior art, the components and the ratios of all raw materials are optimized and the light anti-slipping high-wear-resistance rubber material has the advantages of light weight, anti-slipping performance and wear resistance under the synergistic effect of the components with the ratios. The light anti-slipping high-wear-resistance rubber material is particularly suitable for manufacturing a light and anti-slipping sneaker sole.

Description

technical field [0001] The invention relates to a rubber composite material, in particular to a light-weight, non-slip and highly wear-resistant rubber material used for shoe soles and a preparation method thereof. Background technique [0002] The comfort level, service life, and special functions of shoes are all related to the performance of sole materials to a large extent. Present sole material is in the majority with rubber. Ordinary rubber soles have the advantages of wear resistance, non-slip, elasticity, and waterproof, but they have the disadvantages of heavy weight, non-slip performance that cannot meet high requirements, and poor shock absorption, which cannot meet the needs of strenuous sports. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a new type of light, non-slip and high wear-resistant rubber material, which is used to make shoe soles and has the characteristics of light weight, wear resist...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L7/00C08L9/06C08K13/02C08K3/26C08K3/22C08J9/10A43B13/04
Inventor 丁思博丁思恩郑荣大黄雪琼郑艺文余常彬金校红储晨辉罗显发卢鑫
Owner MAOTAI FUJIAN SOLES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap