Lithium-zinc-titanium-tin series microwave dielectric ceramics material and preparation method thereof
A microwave dielectric ceramic and lithium-zinc technology is applied in the field of new Li2Zn3O8 series microwave dielectric ceramic materials and their preparation to achieve the effect of excellent microwave dielectric properties
Inactive Publication Date: 2013-05-01
TIANJIN UNIV
View PDF1 Cites 13 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, its quality factor needs to be improved, so as to ensure low loss when receiving and transmitting signals
Although the researchers have for Li 2 ZnTi 3 o 8 In-depth research on ceramics, but for Li 2 Zn(Ti 1-x sn x ) 3 o 8 There are no special reports on the preparation and microwave dielectric properties of ceramics
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0017] Will Li 2 CO 3 , ZnO, TiO 2 and SnO 2 Moore Billy 2 CO 3 :ZnO:TiO 2 : SnO 2 =1:1:3(1-x):x (where 0
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Property | Measurement | Unit |
---|---|---|
resonant frequency temperature coefficient | aaaaa | aaaaa |
quality factor | aaaaa | aaaaa |
Login to view more
Abstract
The invention discloses a lithium-zinc-titanium-tin series microwave dielectric ceramics material and a preparation method thereof. A stoichiometric equation is Li2Zn(Ti(1-x)Snx)3O8, wherein x is larger than 0 and is less than or equal to 1. The preparation method comprises the following steps of: compounding Li2CO3, ZnO, TiO2 and SnO2 according to molar ratio; carrying out ball milling; stoving; carrying out presintering at the temperature of 900 DEG C; carrying out secondary ball milling; and sintering at the temperature of 1040-1120 DEG C finally to obtain microwave dielectric ceramics. When x is equal to 0.2, a dielectric constant is 22.1, a resonant frequency temperature coefficient is -22.5ppm / DEG C, and a quality factor reaches 80500 GHz. The preparation method successfully prepares the lithium-zinc-titanium-tin series microwave dielectric ceramics for the first time, and can be applied in a crossing field of microwave dielectric ceramics and multifunctional ceramics.
Description
technical field [0001] The invention belongs to a ceramic composition characterized by composition, in particular to a novel Li 2 Zn(Ti 1-x sn x ) 3 o 8 The invention relates to a microwave dielectric ceramic material and a preparation method thereof. Background technique [0002] At present, in order to obtain practical microwave dielectric ceramic materials, ceramic materials need to meet three requirements: (1) Higher dielectric constant ε r , which is convenient for the miniaturization of the device; (2) high quality factor (Q×f value), ensuring excellent frequency selection characteristics; (3) near-zero resonant frequency temperature coefficient τ f , to ensure stability. [0003] In recent years, researchers have studied SnO 2 For Ba(Zn 1 / 3 Nb 2 / 3 )O 3 and ZnO–TiO 2 The influence of crystal phase and microwave dielectric properties of microwave dielectric ceramics, the research results show that SnO 2 The microwave dielectric properties of dielectric ceram...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/453C04B35/457C04B35/46C04B35/622
Inventor 张平王月华燕波
Owner TIANJIN UNIV
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap