Alginate fiber blended flame-retardant woven fabric and production method
A seaweed fiber and flame retardant technology, which is applied in textile, fiber processing, biochemical fiber processing, etc., can solve the problems of low glass transition temperature, low melting point, poor wear resistance, etc., and achieve soft, breathable, comfortable and skin-friendly fabrics. Good results
Inactive Publication Date: 2014-05-14
山东奈琦尔海洋科技有限公司
View PDF9 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
The disadvantages of polylactic acid fiber are low melting point, low glass transition temperature and poor wear resistance
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 2- Embodiment 4
[0105] According to the method and steps of Example 1, it is made by blending seaweed fiber and corn fiber according to the following weight percentages: 60 / 40 / 0 / 0, 30 / 10 / 30 / 30, 40 / 20 / 20 / 20, 30 / 40 / 30 / 0, 30 / 40 / 0 / 30 are basically the same as embodiment 1 through the technical indicators of the products tested.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| oxygen index | aaaaa | aaaaa |
| oxygen index | aaaaa | aaaaa |
Login to View More
Abstract
The invention relates to an alginate fiber blended flame-retardant bedding fabric and a production method. The alginate fiber blended flame-retardant bedding fabric is characterized by being made from, by weight, 20-60% of alginate fiber, 10-50% of zein fiber, 0-30% of flame-retardant polyester and 0-30% of wool and by means of blended weaving. The production method of the fabric includes four major production process steps of spinning, weaving, printing and dyeing and later period finishing. The alginate fiber blended flame-retardant bedding fabric has a natural intrinsic self-flame-retardant function, and the method is safer and more economic and reliable than traditional flame retardant chemical treatment and chemical fiber flame retardant methods. The fabric is soft to touch, breathable, comfort and good in skin-friendly performance and can be fully degraded as the fibers are natural fibers. Besides, by the aid of different mixed proportions, special requirements in different occasions and under different environments can be met.
Description
technical field [0001] The invention relates to a seaweed fiber blended flame-retardant woven fabric and a production method. Background technique [0002] Seaweed fiber is a new type of natural fiber, which has many incomparable advantages compared to traditional fibers, especially its natural intrinsic flame retardancy. For example, the oxygen index of polyester (the larger the index, the stronger the flame retardancy of the object) is 20, cotton is 18, and seaweed fiber is as high as 34 without any processing, which exceeds the international standard by 6 percentage points, which makes seaweed fiber not ignite an open flame in the air, does not produce molten droplets when burning, and avoids scalding the skin , the product safety is very good, it not only eliminates the high-cost flame retardant, but also does not produce harmful gas after fire like the previous flame retardant materials, it can be said that it is currently the most ideal self-flame retardant material T...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): D03D15/00D03D15/12D02G3/04D06M16/00D06M15/11D03D15/225D03D15/233D03D15/283D03D15/47D03D15/513
Inventor 夏延致姜明鞠海虹
Owner 山东奈琦尔海洋科技有限公司