M56*3 high-strength bolt production method

A technology of high-strength bolts and production methods, applied in the direction of furnaces, heat treatment equipment, heat treatment furnaces, etc., can solve problems such as difficulty in ensuring strength, broken rods, U-turns, etc., and achieve the effect of strong scalability and high hardness

Inactive Publication Date: 2013-06-26
郑州水野大一热处理技术有限公司
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] High-strength bolts are commonly used fasteners in the machinery industry. The current processing method is generally turning and forming, and the strength is often difficult to guarantee. Sometimes unsafe phenomena such as U-turn and rod breakage occur during use, which is harmful to industrial production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • M56*3 high-strength bolt production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0007] In order to make the object, technical solution and advantages of the present invention more clear, the present invention will be further described in detail below in conjunction with the examples. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0008] A production method for M56×3 high-strength bolts, comprising: blanking, forging, rough machining, normalizing, quenching, tempering, finishing, thread processing, and surface chemical treatment; the normalizing temperature is: 870-890 degrees The quenching temperature is: 850-860 degrees; the tempering temperature is: 510-530 degrees. The above-mentioned heat treatment holding time is calculated in the normal way.

[0009] Optionally, the quenching medium is: an inorganic water-based quenching medium.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an M56*3 high-strength bolt production method comprising the steps of blanking, forging, rough processing, normalizing, quenching, tempering, finishing, thread processing, and surface chemical treatment. A normalizing temperature is 870-890 DEG C. A quenching temperature is 850-860 DEG C. A tempering temperature is 510-530 DEG C. With the M56*3 high-strength bolt production method provided by the invention, the produced bolt has high hardness, impact resistance, and high scalability.

Description

technical field [0001] The invention relates to a production method of M56×3 high-strength bolts. Background technique [0002] High-strength bolts are commonly used fasteners in the machinery industry. The current processing method is generally turning and forming, and the strength is often difficult to guarantee. Sometimes unsafe phenomena such as U-turn and rod breakage occur during use, which is harmful to industrial production. Therefore, researching and improving the production method of high-strength bolts to ensure the quality stability of high-strength bolts plays an important role in the development of technology and economy. Contents of the invention [0003] The object of the present invention is to provide a method for producing M56×3 high-strength bolts, the bolts produced have high hardness, impact resistance and strong scalability. [0004] A production method for M56×3 high-strength bolts, comprising: blanking, forging, rough machining, normalizing, quenc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C21D9/00C21D1/18C21D1/28
Inventor 水野长俊
Owner 郑州水野大一热处理技术有限公司
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com