A kind of organosulfur hydrogenation catalyst and its preparation and use method

A hydrogenation catalyst and organic sulfur technology, which is applied in the field of new organic sulfur hydrogenation catalyst and its preparation, can solve the problems of low conversion and removal efficiency of organic sulfides, and achieve the effect of improving conversion efficiency and conversion rate

Active Publication Date: 2017-12-01
BEIJING SJ ENVIRONMENTAL PROTECTION & NEW MATERIAL CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is that when the hydrodesulfurization catalyst in the prior art is used to remove organic sulfides such as thiophene in sulfides, the conversion and removal efficiency of organic sulfides is low, and further provides a A Catalyst for Organosulfur Hydrogenation with High Thiophene Conversion and Removal Efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] The organosulfur hydrogenation catalyst described in this embodiment includes the following components by weight: Al 2 o 3 Carrier, with Al 2 o 3 ZnO, 36g; Iron oxide, counted as Fe is 4g; Molybdenum oxide, counted as molybdenum is 15g; Graphite nanofiber, 12g, the diameter of described graphite nanofiber is 120-140nm, length is 90- 100 μm.

[0049] The preparation method of organic sulfur hydrogenation catalyst described in this embodiment, its steps comprise:

[0050] (1) Configure an acetic acid solution with a mass fraction of 0.39wt%;

[0051] (2) Add ferric nitrate to the above-mentioned acetic acid solution, heat and stir until the precipitate dissolves, and the addition amount of the initial raw material ferric nitrate is 4g as Fe;

[0052] (3) Add ammonium molybdate to the solution prepared in step (2), and add ammonia water to dissolve the precipitate while stirring. The amount of ammonium molybdate added is 15 g in terms of molybdenum, and an active comp...

Embodiment 2

[0057] The organosulfur hydrogenation catalyst described in this embodiment includes the following components by weight: Al 2 o 3 Carrier, with Al 2 o 3 Calculated as 250g; ZnO, 40g; Iron oxide, 5g as Fe; Molybdenum oxide, 18g as molybdenum; Graphite nanofiber, 18g, the diameter of the graphite nanofiber is 120-140nm, and the length is 90- 100 μm.

[0058] Al described in this example 2 o 3 The carrier is prepared from neutralizing material and hydrate with a mass ratio of 1:1.1, wherein the hydrate is prepared from pseudo-boehmite through slurrying and pressure filtration; the preparation method of the neutralizing material is as follows:

[0059] (a) Mix aluminum hydroxide and LiOH with an equivalent concentration of 2:3 and react at 120°C;

[0060] (b) adding acetic acid to the solution prepared in step (a) for neutralization;

[0061] (c) Taking out the product generated after being neutralized by the acetic acid, washing with water, and pressing to obtain a neutral...

Embodiment 3

[0071] The organosulfur hydrogenation catalyst described in this embodiment includes the following components by weight: Al 2 o 3 Carrier, with Al 2 o 3ZnO, 44g; Iron oxide, 6g as Fe; Molybdenum oxide, 21g as molybdenum; Graphite nanofiber, 15g, the diameter of the graphite nanofiber is 120-140nm, and the length is 90- 100 μm.

[0072] Al described in this example 2 o 3 The carrier is prepared from neutralizing material and hydrate with a mass ratio of 1:1.2, wherein the hydrate is prepared from pseudo-boehmite through slurrying and pressure filtration; the preparation method of the neutralizing material is as follows:

[0073] (a) Mix aluminum hydroxide and KOH with an equivalent concentration ratio of 2:4 and react at 150°C;

[0074] (b) adding citric acid to the solution prepared in step (a) for neutralization;

[0075] (c) Taking out the product generated after neutralization by the citric acid, washing with water and pressure filtering to obtain a neutralized mater...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a kind of organosulfur hydrogenation catalyst, it comprises Al2O3 carrier of specific weight, ZnO, iron oxide and molybdenum oxide and graphite nanofiber, and the diameter of described graphite nanofiber is 120-140nm, and length is 90-90nm 100 μm. The organosulfur hydrogenation catalyst in the present invention effectively improves the conversion efficiency of thiophene by adding graphite nanofibers and synergizing with other active metal components. As a material capable of absorbing hydrogen, the graphite nanofibers have a surface with A large number of adsorption sites capable of storing hydrogen. Hydrogen molecules are adsorbed on the surface of the graphite nanofibers. During hydrogenation catalysis, the active hydrogen atoms located on the surface of the graphite nanofibers and between the active metal components can be hydrogenated more effectively. Thiophene compounds, thereby increasing the conversion rate of thiophene.

Description

technical field [0001] The invention relates to a novel organic sulfur hydrogenation catalyst and a preparation method thereof, belonging to the technical field of desulfurizers. Background technique [0002] my country is the largest country in coke production and export. With the continuous improvement of my country's economic level, the coke industry has developed rapidly. However, in the coking process, a large amount of by-product coke oven gas will be produced, and coke oven gas contains H 2 S, CS 2 , thiophene and other harmful impurities, these impurities not only corrode the equipment, block the pipeline, but also lead to the deactivation of the catalyst and affect the catalytic effect. where H 2 S is the most typical impurity, and thiophene is one of the sulfides with the highest chemical stability and the most difficult to remove. Therefore, how to improve the conversion rate of organic sulfur hydrogenation catalysts to thiophene, increase the service life of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/881C10K1/34
Inventor 赵文涛刘彦芳郭玉峰
Owner BEIJING SJ ENVIRONMENTAL PROTECTION & NEW MATERIAL CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com