Super strong high phosphorus boron cast iron

A high-phosphorus-boron, cast iron technology, applied in the field of cast iron, can solve the problems of affecting the service life of the whole machine, being too soft and not wear-resistant, and the cast iron is easy to be damaged, so as to achieve the effects of long life, good wear resistance and improved economic benefits

Active Publication Date: 2015-11-04
威佰昇科技(台州)有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The cast iron of the existing automobile air compressor cylinder is either too hard and easy to damage, or too soft and not wear-resistant, which affects the service life of the whole machine, high energy consumption, and poor stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Super strong high phosphorus boron cast iron
  • Super strong high phosphorus boron cast iron
  • Super strong high phosphorus boron cast iron

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] The formula seasoning is (percentage by weight):

[0011] C: 3.1%; S: 0.05%; Si: 1.7%; P: 0.3%; Cr: 0.3%; Mn: 0.8%; B: 0.15%, and the rest is molten iron.

[0012] according to figure 1 The process shown was carried out.

Embodiment 2

[0014] The formula seasoning is (percentage by weight):

[0015] C: 3.2%; S: 0.08%; Si: 1.8%; P: 0.23%; Cr: 0.3%; Mn: 0.7%; B: 0.1%, and the rest is molten iron.

[0016] according to figure 1 The process shown was carried out.

Embodiment 3

[0018] The formula seasoning is (percentage by weight):

[0019] C: 3.3%; S: 0.1%; Si: 2%; P: 0.22%; Cr: 0.1%; Mn: 0.6%; B: 0.08%, and the rest is molten iron.

[0020] according to figure 1 The process shown was carried out.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides super-strong high-phosphorus boron cast iron. The super-strong high-phosphorus boron cast iron is made from molten iron and ingredients and is characterized in that the ingredients comprise the following raw materials in percentage by weight: 2.5-4% of C, 0-0.1% of S, 1.5-2.5% of Si, 0.2-0.4% of P, 0.05-0.5% of Cr, 0.5-1% of Mn and 0.05-0.2% of B. The super-strong high-phosphorus boron cast iron has the advantages that the abrasive resistance is good; the complete machine is durable in use and long in life; the economic benefit is increased; in the meantime, the energy consumption is low and the stability is good; virtuous circle is formed among components; the energy is saved and the emission is reduced; the boron cast iron is suitable for cutting machining; the machining indexes achieve the design standard; and the best adaptation performance is shown between the boron cast iron and a piston ring.

Description

technical field [0001] The invention belongs to the field of cast iron, in particular to a super-strong high-phosphorus-boron cast iron. Background technique [0002] The cast iron of the cylinder block of the existing automobile air compressor is either too hard and easy to damage, or too soft and not wear-resistant, which affects the service life of the whole machine, high energy consumption, and poor stability. Contents of the invention [0003] In order to solve the above technical problems, the present invention provides a super-strong high-phosphorus-boron cast iron. [0004] A super-strength high-phosphorus-boron cast iron prepared from molten iron and a formula seasoning, characterized in that the weight percentage of each raw material in the formula seasoning to the total weight of the molten iron and the formula seasoning is: C: 2.5-4%; S: 0-0.1%; Si: 1.5-2.5%; P: 0.2-0.4%; Cr: 0.05-0.5%; Mn: 0.5-1%; B: 0.05-0.2%. [0005] The super-strong high-phosphorus-boron...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C37/10
Inventor 江新军
Owner 威佰昇科技(台州)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com