Flame retardant and acid and alkali-resistant plastic containing 1,4-pentadiene
A technology of pentadiene and acid and alkali resistance, applied in the direction of coating, etc., can solve the problems of plastic flame retardancy and poor acid and alkali resistance, and achieve good flame retardancy and acid and alkali resistance effects
Active Publication Date: 2013-09-11
江苏悠谷未来科技有限公司
View PDF1 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0003] The technical problem to be solved: the problem of poor flame retardancy and acid and alkali resistance of conventional plastics
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0010] At 60°C, put the ingredients of Example 1 in Table 1 into the reaction container according to their weight, stir well, heat to 200°C and keep for 8 hours, and after cooling, a plastic with good flame retardant, acid and alkali resistance can be obtained.
Embodiment 2
[0012] The difference from Example 1 is that the initial heating temperature is 80°C.
Embodiment 3
[0014] The difference with Example 1 is that the cooling time after stirring is 10h.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention relates to a flame retardant and acid and alkali-resistant plastic containing 1, 4-pentadiene. The plastic comprises the following components: by weight, 40-50 parts of the 1, 4-pentadiene, 30-40 parts of isobutene, 30-40 parts of cellulose acetate, 10-20 parts of calcium oxide, 10-20 parts of boron oxide, 10-20 parts of polyethersulfone resin and 10-20 parts of carbon black. The prepared plastic containing the 1,4-pentadiene has good effects of flame retardance and acid and alkali resistance.
Description
technical field [0001] The invention relates to a flame-retardant acid-alkali-resistant plastic, in particular to a flame-retardant acid-alkali-resistant plastic containing 1,4-pentadiene. Background technique [0002] In the process of industrial development, in the subdivision of flame-retardant acid-alkali-resistant plastics, users have increasingly high requirements for flame-retardant acid-alkali-resistant plastics. For example, more and more attention is paid to the flame-retardant properties of plastics. Having flame retardant properties can solve a lot of technical problems. At the same time, we are also very concerned about the acid and alkali resistance of plastics. Plastics with good flame retardant properties and acid and alkali resistance are widely used, but currently there are flame retardant properties on the market. There are very few types of plastics with good flame retardancy and acid and alkali resistance, so developing a plastic with good flame retardan...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More IPC IPC(8): C08F291/14C08F291/06C08F236/20C08F210/10C08K3/22C08K3/38C08K3/04C09D4/06C09D7/12
Inventor 张卫蒋学功张美英
Owner 江苏悠谷未来科技有限公司