Fitting layer for improving moisture permeability of fitting fabric and preparation method of fitting layer

A technology for laminating fabrics and laminating layers, which is applied in textiles, papermaking, fiber processing, etc. It can solve the problems of lowering the moisture permeability of fabrics, low waterproof and moisture permeability of the primer layer, and failure to keep warm, waterproof, and moisture permeability. To achieve the effect of improving the bonding strength

Active Publication Date: 2013-10-02
TRYD TEXTILE FIBER TECH
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current laminated fabrics are mainly 20K/20K. This laminated fabric already has good waterproof and moisture-permeable properties, but it still cannot achieve warmth, waterproof and moisture-permeable properties in some relatively extreme or harsh environments. Require
Research on the current lamination products found that in the lamination layer, the waterproof and moisture-permeable performance of the top rubber layer is high, but the waterproof and moisture-permeable perform

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fitting layer for improving moisture permeability of fitting fabric and preparation method of fitting layer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A bonding layer that improves the moisture permeability of a bonding fabric, the bonding layer includes a primer layer and a surface layer, wherein the weight ratio of the primer layer is: 100 parts of two-component polyurethane resin, 10 parts Primer solvent, 1 part of polyisocyanate bridging agent, 0 part of accelerator, 5 parts of one-component polyurethane additive, 5 parts of one-component moisture-reactive PUR additive, 0 part of softener and anti-tearing agent. The weight ratio of the components of the two-component polyurethane resin is as follows: 40 parts of polyurethane resin, 25 parts of dimethylformamide, 40 parts of ethyl acetate, and 18 parts of toluene. The appearance layer of the two-component polyurethane resin is light yellow and translucent, the non-volatile component: 45±1.5, and the 100% modulus: 2-3MPa. The weight ratio of each component of the one-component moisture-reactive PUR additive is: 60 parts of polyurethane resin, 10 parts of toluene, an...

Embodiment 2

[0055] The bonding layer in this embodiment includes a primer layer and a surface rubber layer, wherein the weight ratio of the primer layer is: 100 parts of two-component polyurethane resin, 50 parts of primer solvent, 10 parts of polyisocyanate Bridging agent, 5 parts of accelerator, 30 parts of one-component polyurethane additive, 20 parts of one-component moisture-responsive PUR additive, 5 parts of softener and anti-tearing agent. The weight ratio of the components of the two-component polyurethane resin is as follows: 45 parts of polyurethane resin, 35 parts of dimethylformamide, 50 parts of ethyl acetate, and 25 parts of toluene. The appearance layer of the two-component polyurethane resin is light yellow and translucent, the non-volatile component: 45±1.5, and the 100% modulus: 2-3MPa. The weight proportion of each component of the one-component moisture-reactive PUR additive is: 80 parts of polyurethane resin, 30 parts of toluene, and 20 parts of ethyl acetate. The r...

Embodiment 3

[0063] The bonding layer in this embodiment includes a primer layer and a surface rubber layer, wherein the weight ratio of each component of the primer layer is: 100 parts of two-component polyurethane resin, 25 parts of primer solvent, and 5 parts of polyisocyanate Bridging agent, 3 parts of accelerator, 15 parts of one-component polyurethane additive, 10 parts of one-component moisture-reactive PUR additive, 3 parts of softener and anti-tearing agent. The weight ratio of the components of the two-component polyurethane resin is: 42 parts of polyurethane resin, 33 parts of dimethylformamide, 45 parts of ethyl acetate, and 22 parts of toluene. The appearance layer of the two-component polyurethane resin is light yellow and translucent, the non-volatile component: 45±1.5, and the 100% modulus: 2-3MPa. The weight ratio of each component of the one-component moisture-reactive PUR additive is: 78 parts of polyurethane resin, 16 parts of toluene, and 6 parts of ethyl acetate. The...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a fitting layer for improving the moisture permeability of a fitting fabric and a preparation method of the fitting layer. The fitting layer comprises a bottom adhesive layer and a surface adhesive layer, wherein the bottom adhesive layer comprises the following components by weight ratio: 100 parts of double-liquid type polyurethane resin, 10-50 parts of a bottom adhesive solvent, 1-10 parts of a polyisocyanate bridging agent, 0-5 parts of an accelerator, 5-30 parts of a one-liquid type polyurethane addition agent, 5-20 parts of a single-component moisture reactive polyurethane (PUR) addition agent and 0-5 parts of a softening agent and a tear-resistant agent; the surface adhesive layer comprises the following components by ratio: 100 parts of one-liquid type polyether polyurethane resin, 10-50 parts of a surface adhesive solvent, 0-2 parts of a release agent and 0-5 parts of a wax synthetic amorphous silica antisticking agent. By utilizing the fitting layer, the moisture-permeable and water-proof property of the fitting fabric reaches 40K/20K.

Description

technical field [0001] The invention relates to the technical field of textiles, in particular to a bonding layer used on a bonding fabric to improve the moisture permeability of the bonding material and a preparation method thereof. Background technique [0002] Fitting fabric refers to setting a fitting layer on the fabric, and using the performance of the fitting layer to endow the fabric layer with new functions. The general bonding layer includes a top rubber layer and a bottom rubber layer, and the bottom rubber layer must have sufficient adhesion to closely fit the top rubber layer and the fabric layer. Due to the addition of the fitting layer, the moisture permeability of the fitting fabric is an important parameter to measure the performance of the fitting fabric. The current laminated fabrics are mainly 20K / 20K. This laminated fabric already has good waterproof and moisture-permeable properties, but it still cannot achieve warmth, waterproof and moisture-permeable...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M15/564D06M15/568D06M11/79
Inventor 李肇魁李健徐广刘介正陈雅
Owner TRYD TEXTILE FIBER TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap