Resin asphalt ultraviolet aging testing equipment and testing method thereof

A technology of resin asphalt and aging test, which is applied to the preparation of test samples and the use of stable bending force to test the strength of materials, etc. It can solve the problems of inability to perform resin asphalt aging test, and achieve simple structure, high test accuracy and convenient operation Effect

Inactive Publication Date: 2015-02-25
HARBIN INST OF TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the problem that the aging test of resin asphalt cannot be carried out by using xenon arc lamp or open carbon arc lamp, and propose a method for ultraviolet aging test of resin asphalt

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Resin asphalt ultraviolet aging testing equipment and testing method thereof
  • Resin asphalt ultraviolet aging testing equipment and testing method thereof
  • Resin asphalt ultraviolet aging testing equipment and testing method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0018] Specific implementation mode one: combine figure 1 and figure 2 Describe this embodiment, this embodiment comprises ultraviolet aging incubator 1, lamp frame 2 and four ultraviolet lamp tubes 4, the front of ultraviolet aging incubator 1 is the box door 1-2 that opens in opposite directions, the top of ultraviolet aging incubator 1 Ventilation holes 1-1 are provided for connecting the lamp tube wire 6 with an external power supply. The lamp frame 2 is set in the ultraviolet aging incubator 1, and four ultraviolet lamp tubes 4 are horizontally fixed on the top of the lamp frame 2, two adjacent The distance t between the ultraviolet lamp tubes 4 is 65 mm to 75 mm. Four ultraviolet lamp tubes 4 are arranged in parallel through wires, and each ultraviolet lamp tube 4 has its matching ballast 5 and wires 6 . The ultraviolet lamp 4 adopts a UVA-340 lamp, its ultraviolet wavelength is 290-400nm, its power is 40W, and its ultraviolet irradiance is 40.62W / m2.

specific Embodiment approach 2

[0019] Specific implementation mode two: combination figure 2 The present embodiment will be described. The pitch t of the ultraviolet lamp tubes 4 in the present embodiment is 70 mm. Other connection relationships are the same as those in the first embodiment.

specific Embodiment approach 3

[0020] Specific implementation mode three: combination image 3 This embodiment is described. The difference between this embodiment and the third embodiment is that it also has an exhaust fan 3 installed on the side wall of the ultraviolet aging thermostat 1 . Exhaust fan 3 is used for air exchange inside and outside the box to ensure the temperature and humidity balance in the box. Other connections are the same as those in the first or second specific embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses resin asphalt ultraviolet aging testing equipment and a testing method thereof and relates to resin asphalt aging testing equipment and a method which aim at solving the problem that an aging test can not be carried out on resin asphalt by adopting an xenon arc lamp or an open type carbon arc lamp. According to the resin asphalt ultraviolet aging testing equipment, a lamp bracket is arranged in an ultraviolet aging incubator, and four ultraviolet lamp tubes are horizontally fixed at the top of the lamp bracket and arranged in parallel through electric wires. The testing method comprises the steps of: 1, preparation of a test piece, namely a. preparation of a resin asphalt test piece; b. preparation of a resin asphalt concrete Marshall test piece; c. preparation of a resin asphalt concrete small beam test piece; 2, putting all aging groups into the ultraviolet aging incubator; putting room temperature groups into a room; 3, after 21 days, taking out all the aging groups; 4, a. carrying out infrared spectrum analysis on the resin asphalt test piece; b. testing the stability of the resin asphalt concrete Marshall test piece; c. carrying out a bending test on the resin asphalt concrete small beam test piece. The resin asphalt ultraviolet aging testing equipment and the testing method thereof are used for the resin asphalt aging tests.

Description

technical field [0001] The invention relates to a resin asphalt aging test method, in particular to a resin asphalt ultraviolet aging test method. Background technique [0002] At present, relevant specifications and standards for photoaging test methods are mainly formulated based on the International Organization for Standardization (ISO) light test methods for plastic materials. Domestically, there are GBT14522 (artificial weathering test methods for plastics, coatings, and rubber materials used in machinery industry products), GBT16422 (light source exposure test methods for plastic laboratories), etc., and the United States has ASTM G154-06 (Standard Practice for Operating Fluorescent Light Apparatus for UV Exposure of Nonmetallic Materials) and so on. The recommended light sources include xenon arc lamps, fluorescent ultraviolet lamps, open carbon arc lamps, etc. In China, high-pressure mercury lamps are also used for ultraviolet aging tests. Since the above-mentione...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N3/20G01N1/44
Inventor 唐浩许勐荆儒鑫冯德成
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com