Amino functionalized ionic liquid/hydrotalcite-like compound composite material, and preparation method and application thereof

A technology of amino functionalization and ionic liquid, applied in chemical instruments and methods, adsorption water/sewage treatment, water/sludge/sewage treatment, etc.

Active Publication Date: 2013-11-20
日照经济技术开发区客商服务有限公司
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

So far, the preparation of amino-functionalized ionic liquids and hydrotalcite-like composites by co-precipitation method and its application in organic pollutant

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Amino functionalized ionic liquid/hydrotalcite-like compound composite material, and preparation method and application thereof
  • Amino functionalized ionic liquid/hydrotalcite-like compound composite material, and preparation method and application thereof
  • Amino functionalized ionic liquid/hydrotalcite-like compound composite material, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] (a) Preparation of amino-functionalized ionic liquid 1-methyl-3-aminoethylimidazolium tetrafluoroborate

[0034] Under ice-bath conditions, pipette 20 mL of N-methylimidazole (10.3 g, 0.25 mol) into a round-bottomed flask, and add equimolar 2-bromoethylamine hydrobromide (51.22 g, 0.25 mol) under constant stirring It was slowly added dropwise into absolute ethanol (20 mL) equal to the volume of N-methylimidazole, and the reaction solution was stirred at 50° C. for 24 hours, and protected by nitrogen gas during the reaction. After the reaction, remove the solvent and unreacted volatile substances by rotary evaporation, dissolve the product with a small amount of water, then add 250 mL of 1 mol / L potassium hydroxide solution to reduce the protected amino group, and remove most of the water in the resulting solution by distillation under reduced pressure Then vacuum-dry at 60°C to constant weight, dissolve the product with ethanol-tetrahydrofuran mixed solvent with a volum...

Embodiment 2

[0038] (a) Preparation of amino-functionalized ionic liquid 1-methyl-3-aminoethylimidazolium tetrafluoroborate

[0039] Adopt the method and the condition synthesis of step (a) among the embodiment 1;

[0040] (b) Preparation of amino-functionalized ionic liquid / hydrotalcite-like composites

[0041] Divalent metal salt Zn(NO 3 ) 2 and trivalent metal salt Al(NO 3 ) 3 Prepare a mixed salt solution at a molar ratio of 2:1, the total metal ion concentration is 0.6 mol / L, and then the ionic liquid is 1-methyl-3-aminoethylimidazolium tetrafluoroborate and divalent metal salt Zn(NO 3 ) 2 Add the molar ratio of 0.5:2 into the mixed salt solution, titrate the above mixed solution and the sodium hydroxide solution with a molar concentration of 2 mol / L at the same time, control the pH between 9.0 and 10.0, stir vigorously, and age at 80 °C for 8 Hour. The obtained slurry was suction-filtered, the filter cake was washed 4 times with distilled water, and dried at 60° C. for 24 hou...

Embodiment 3

[0043] (a) Preparation of amino-functionalized ionic liquid 1-methyl-3-aminoethylimidazolium tetrafluoroborate

[0044] Adopt the method and the condition synthesis of step (a) among the embodiment 1;

[0045] (b) Preparation of amino-functionalized ionic liquid / hydrotalcite-like composites

[0046] Divalent metal salt Zn(NO 3 ) 2 and trivalent metal salt Al(NO 3 ) 3 Prepare a mixed salt solution at a molar ratio of 2:1, the total metal ion concentration is 0.6 mol / L, and then the ionic liquid is 1-methyl-3-aminoethylimidazolium tetrafluoroborate and divalent metal salt Zn(NO 3 ) 2 The molar ratio of 0.8:2 was added to the mixed salt solution, and the above mixed solution and the ammonia solution with a molar concentration of 4 mol / L were titrated simultaneously to control the pH between 9.0 and 10.0, vigorously stirred, and aged at 50°C for 18 hours. The obtained slurry was suction-filtered, the filter cake was washed 4 times with distilled water, and dried at 60° C. f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses an amino functionalized ionic liquid/hydrotalcite-like compound composite material, and a preparation method and an application thereof. The preparation method comprises: firstly synthesizing an amino functionalized ionic liquid, then taking amino functionalized ionic liquid with different molar masses, employing a coprecipitation method to load the ionic liquid on the surface of the hydrotalcite-like compound, to prepare the amino functionalized ionic liquid/hydrotalcite-like compound composite material with a lamellar structure. The prepared organic-inorganic composite material has the structure and performance advantages of the functionalized ionic liquid and the hydrotalcite-like compound; the composite material, as an absorbent, shows good adsorption removal capability on pollutions such as o-chlorophenol , m-chlorophenol or p-chlorophenol in water, and has substantially better adsorptivity performance than the hydrotalcite-like compound; and the synergy advantage of the amino functionalized ionic liquid and the hydrotalcite-like compound is given a full play.

Description

Technical field [0001] The invention involves a composite material of amino -functional ionic liquid / type of water talcium; the present invention also involves the preparation method of the composite material and its application in removing pollutants in the water body. Background technique [0002] Water -type talc (abbreviated LDH) is a type of two -dimensional nanocometer clay, which can be expressed as [M 1-x 2+ M x 3+ (OH) 2 ] x+ (A n- Cure x / n · Mh 2 O, where M 2+ Refers to the two -price metal cation, M 3+ Refers to the three -valent metal cation, x is M 2+ M 3+ Moorebi, A n- It is a stable anion that can be stabilized between layers, and has a water -like structured structure. Due to the advantages of the composition of the layer layer and the adjustment of the charging density, the interlayer object molecules, the crystal size, and the low biological toxicity, it has been organic catalytic, which is already organic catalytic,Polymer additives, biomedicine, environmenta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J20/22B01J20/30C02F1/28C02F101/36
Inventor 詹天荣侯万国徐 洁王新军
Owner 日照经济技术开发区客商服务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap