Rubber tire tread and milling process thereof

A technology for rubber tires and treads, applied in the field of tire manufacturing, can solve problems such as loss of use value and loss, and achieve the effects of excellent ozone resistance, slow migration speed, and good vulcanization flatness.

Inactive Publication Date: 2015-04-15
SHANDONG YONGTAI CHEM GROUP
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the processing, storage and use of rubber or rubber products, due to the influence of various external factors, they gradually lose their original excellent properties, so that they lose their use value in the end.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment １

[0034] A kind of rubber tire tread of the present invention comprises the following components by weight:

[0035] Natural rubber 100 SBR 10

[0036] Tread rubber powder 10 Stearic acid 2

[0037] Sulfur powder 1.4 White carbon black 14

[0038] Carbon black N220 12 Aromatic oil 6

[0039] Zinc oxide 2 Antiaging agent 6

[0040] Pine tar 1 Accelerator 1.3

[0041] Anti-reversion agent 0.2 Binder 3.

[0042] Natural rubber is smoked film.

[0043] The anti-aging agent includes 30% anti-aging agent RD, 30% anti-aging agent 4020, 30% anti-aging agent 3100 and 10% type B microcrystalline wax.

[0044] The accelerator consists of 50% accelerator DM and 50% accelerator CZ.

[0045]The anti-reversion agent is PK900.

[0046] The adhesive is petroleum tackifying resin.

[0047] The mixing process of the rubber tire tread adopts a three-stage mixing process:

[0048] The first stage: bake styrene-butadiene rubber and natural rubber to a temperature of 35°C in a rubber drying ...

Embodiment 2

[0052] A kind of rubber tire tread of the present invention comprises the following components by weight:

[0053] Natural rubber 110 SBR 10

[0054] Tread rubber powder 20 Stearic acid 2.5

[0055] Sulfur powder 2 Silica 18

[0056] Carbon black 15 Aromatic oil 26

[0057] Zinc oxide 7 Antiaging agent 7

[0058] Pine Tar 3 Accelerator 3

[0059] Anti-reversion agent 0.9 Adhesive 5.

[0060] The natural rubber is chlorinated natural rubber.

[0061] Carbon black is carbon black N220.

[0062] The anti-aging agent includes 10% anti-aging agent RD, 20% anti-aging agent 4020, 62% anti-aging agent 3100 and 8% type B microcrystalline wax.

[0063] The accelerator consists of 90% accelerator DM and 10% accelerator CZ.

[0064] The anti-reversion agent is PK900.

[0065] The adhesive is petroleum tackifying resin.

[0066] The mixing process of the rubber tire tread adopts a three-stage mixing process:

[0067] The first stage: bake styrene-butadiene rubber and natural rub...

Embodiment 3

[0071] A kind of rubber tire tread of the present invention comprises the following components by weight:

[0072] Natural rubber 90 SBR 0

[0073] Tread rubber powder 15 Stearic acid 1.5

[0074] Sulfur powder 1.7 White carbon black 16

[0075] Carbon black 13 Aromatic oil 11

[0076] Zinc oxide 3 Antiaging agent 5

[0077] Pine Tar 4 Accelerator 1.5

[0078] Anti-reversion agent 0.4 Binder 3.

[0079] Natural rubber is a mixture of smoked rubber sheet, white crepe rubber sheet, granular rubber, rubber clear crepe sheet, and chlorinated natural rubber.

[0080] The carbon black is carbon black N330.

[0081] The anti-aging agent includes 20% anti-aging agent RD, 20% anti-aging agent 4020, 56% anti-aging agent 3100 and 4% type B microcrystalline wax.

[0082] The accelerator consisted of 40% accelerator DM and 60% accelerator CZ.

[0083] The anti-reversion agent is PK900.

[0084] The adhesive is petroleum tackifying resin.

[0085] The mixing process of the rubber ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rubber tire tread and a mixing process thereof. The tread rubber comprises the following components in parts by weight: natural rubber 70-110, styrene-butadiene rubber 0-15, tread rubber powder 5-20, hard Fatty acid 1.5-2.5, sulfur powder 1-2, white carbon black 2-18, carbon black 12-15, aromatic oil 2-30, zinc oxide 1-8, antioxidant 4-7, pine tar oil 1-4, promote Agent 1-4, anti-reversion agent 0.2-1, adhesive 2-5; adopting three-stage mixing process, the present invention can improve the wear resistance, tear resistance and anti-collapsing performance of the tire tread .

Description

technical field [0001] The invention belongs to the technical field of tire manufacturing, and in particular relates to a rubber tire tread and a mixing process thereof. Background technique [0002] As an important part of the car, the car tire is an important part of the car to bear gravity, transmit traction force, braking force, steering force and bear the reaction force of the road surface. Its quality is directly related to personal and property safety. [0003] It is customary in the world to divide car tires into passenger car tires (Passenger Car Tire) and light truck tires (LightTruck Tire), in addition to truck and bus tires (Truck&Bus Tire); ) and radial tires (Radil), and radial tires are divided into two types: all-steel and semi-steel. Generally, truck and bus radial tires with specifications above 9.00 are called all-steel radial tires, and trucks, bus tires and cars with specifications below 9.00 Radial tires are called semi-steel radial tires. [0004] Ge...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L7/00C08L9/06C08K13/02C08K3/36C08K3/04C08K3/06C08K5/3437C08K5/18B60C1/00B29B7/28
Inventor 尤晓明冯小波邓士海徐丽花张国栋王显涛延云峰魏文祥
Owner SHANDONG YONGTAI CHEM GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com