Ageing heat treatment process of 3003 aluminium alloy electronic foil

A technology of aging heat treatment and aluminum alloy, which is applied in the field of aging heat treatment process of 3003 aluminum alloy electronic foil, can solve the problem of not performing aging heat treatment, etc., and achieve the effect of improving specific capacitance and good corrosion effect.

Active Publication Date: 2013-12-18
威海海鑫新材料有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although 3003 aluminum alloy is an alloy that cannot be strengthened by heat

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Example 1 3003 hot-rolled billet plan:

[0013] 1) Hot rolled from hot rolled billet to , homogenizing annealing is performed at this thickness, and the annealing mechanism is .

[0014] 2) After four times of cold rolling (after the first pass of cold rolling is , after the second cold rolling pass is , after the third pass of cold rolling is , after the fourth pass of cold rolling is ) process, the thickness, carry out Fully annealed process.

[0015] 3) Continue cold rolling to , and then converted to foil rolling production, after three foil rollings (after the first foil rolling is , after the second foil rolling is , after the third foil rolling is ) process, the thickness, carry out Artificial aging.

[0016] 4) After three times of foil rolling (after the first foil rolling, , after the second foil rolling is , the third foil rolling can be selected to generate according to specific needs Aluminum foil with different thickness ...

Embodiment 2

[0020] Example 2 3003 casting and rolling billet plan:

[0021] 1) Hot rolled from cast billet to , homogenizing annealing is performed at this thickness to make the structure uniform and reduce segregation. The annealing mechanism is .

[0022] 2) After five passes of cold rolling (after the first pass of cold rolling is , after the second cold rolling pass is , after the third pass of cold rolling is , after the fourth pass of cold rolling is , after the fifth pass of cold rolling is ) process, the thickness, carry out Complete annealing process to reduce the residual stress of the tissue.

[0023] 3) Continue cold rolling to , and then converted to foil rolling production, after two foil rollings (after the first foil rolling is , after the second foil rolling is ) process, the thickness, carry out Artificial aging.

[0024] 4) After three times of foil rolling (after the first foil rolling, , after the second foil rolling is , the third foil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Provided is an ageing heat treatment process of a 3003 aluminium alloy electronic foil. When original hot rolling or cast rolling blank is rolled to be in the thickness of 5.0<+/-0.2>mm, high temperature homogenizing annealing treatment is used, the formation is well-closed, and segregation is weakened. Multi-pass cold rolling is continuously conducted after annealing, and when the thickness of 0.5<+/-0.05>mm is achieved, a complete annealing treatment process is conducted to weaken residual stress. The multi-pass cold rolling is continuously conducted until the thickness of 0.24<+/-0.01>mm is achieved, foil rolling is directly converted, when multi-pass foil rolling reaches the thickness of 0.09<+/-0.005>mm, ageing treatment of 80<+/-5> DEG C *3<+/-0.5> h is conducted, and the control over the morphology and the distribution of the second phase of the aluminium alloy electronic foil blank is achieved. The thickness of a finished product of 0.042mm - 0.038mm is achieved through multiple times of foil rolling after the ageing treatment. A specified heat treatment process is conducted on the 3003 aluminium alloy electronic foil blank, the control over the morphology and the distribution of second phase particles (MnAl6 phase) in the 3003 aluminium alloy is achieved, a large number of second phase particles are made to be dispersed and distributed evenly, the blank is used, the corrosion effect in the later period is good, the specific capacitance of the aluminium alloy electronic foil is improved, and 560-595 muF/cm<2> can be achieved.

Description

technical field [0001] The invention relates to an aging treatment method for a 3003 aluminum alloy electronic foil blank, mainly for producing Aging heat treatment process for electronic aluminum foil blanks for aluminum electrolytic capacitors with high thickness. Background technique [0002] Aluminum foil is widely used in various fields such as electrical appliances, packaging, and construction. With the development of the times, the application range has also increased, and higher requirements have been put forward for product quality. 3003 aluminum alloy electronic foil is an aluminum foil widely used in aluminum electrolytic capacitors. Due to the rapid development of electronic machines in the direction of short, small, light and thin, the process of miniaturization and miniaturization of aluminum electrolytic capacitors must be accelerated. The key to the miniaturization of aluminum capacitors lies in the large effective surface area of ​​the aluminum electrode ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22F1/04
Inventor 黄元春杜志勇朱弘源肖政兵刘宇
Owner 威海海鑫新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap