A kind of tungsten-doped diamond-like coating and preparation method thereof

A technology of diamond coating and diamond layer, applied in the direction of metal material coating process, coating, metal layered products, etc., can solve the problems that cannot be completely eliminated, poor surface roughness, etc., and achieve good oxidation resistance and chemical stability , good oxidation resistance, wear resistance and friction reduction performance, and low friction coefficient

Inactive Publication Date: 2015-08-26
XI AN JIAOTONG UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the limitations of the preparation principle itself, the droplets in the arc ion plating coating cannot be completely eliminated, resulting in a loose coating structure and poor surface roughness.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of tungsten-doped diamond-like coating and preparation method thereof
  • A kind of tungsten-doped diamond-like coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Embodiment 1 provides a kind of method for preparing tungsten-doped diamond-like coating on the surface of high-speed steel. It should be noted that the tungsten-doped diamond-like coating prepared by the method of the present invention can be used on any black or non-ferrous metal material surface carried out above, not limited to this example.

[0031] Example 1

[0032] (1) Substrate pretreatment: use high-speed steel substrate with hardness HRC=60 after quenching at 1170°C and tempering at 550°C (material: W 18 Cr 4 V) As a substrate, its surface is degreased and polished, then immersed in acetone for ultrasonic cleaning, and then dehydrated with alcohol.

[0033] (2) Put the pretreated substrate on the turret rod in the vacuum chamber of the arc and magnetron sputtering composite coating equipment. Such as figure 1 As shown, the arc and magnetron sputtering composite coating equipment at least includes a vacuum chamber 1, a turret 2, a bias voltage 3, a turret ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
hardnessaaaaaaaaaa
anti-oxidation temperatureaaaaaaaaaa
Login to View More

Abstract

The invention provides a wolframium (W) doped diamond-like coating and a preparation method thereof. The coating comprises a Cr bottom layer, a CrC transition layer and a W doped diamond-like layer, wherein the Cr bottom layer is deposited on the surface of a substrate, the CrC transition layer is prepared on the Cr bottom layer, and the W doped diamond-like layer is prepared on the CrC transition layer. The preparation method comprises the following steps: firstly carrying out plasma cleaning on the substrate, opening a column electric arc Cr target to prepare the Cr bottom layer on the surface of the substrate, opening a plane magnetron sputtering C target to prepare the CrC transition layer on the Cr bottom layer, and finally closing the column electric arc Cr target and opening a plane magnetron sputtering W target to prepare the W doped diamond-like layer on the CrC transition layer. According to the preparation method provided by the invention, the electric arc and magnetron sputtering composite coating technology is adopted, so that the prepared coating is smooth and compact in surface, high in hardness, high in film bonding strength, low in friction coefficient and good in oxidization resistance and chemical stability, and can meet relatively high requirements for oxidization resistance, wear resistance and antifriction performance, therefore the coating has wide application prospects.

Description

technical field [0001] The invention belongs to the field of coating material preparation, in particular to a tungsten-doped diamond-like carbon (DLC) coating and a preparation method thereof. Background technique [0002] Traditional carbon-based superhard coatings, such as Ti-doped or Cr-doped diamond-like carbon (DLC) coatings have excellent properties such as high hardness and low friction coefficient, and are widely used in the field of surface protection of mechanical parts prospects, but the insufficient oxidation resistance of these coatings has limited their further applications. In recent years, in order to reduce the fuel consumption of automobile and motorcycle engines, it is becoming more and more important to solve the wear and oxidation failure of engine sliding parts such as pistons, piston rings and cylinders under high temperature working conditions. In addition, the surfaces of high-speed moving parts such as refrigeration compressor crankshafts and slide...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C14/34C23C14/35C23C14/06B32B15/04B32B9/04
Inventor 马胜利
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products