Abrasion-resistant steel plate excellent in stress corrosion cracking resistance and manufacturing method thereof

一种制造方法、耐磨损的技术,应用在耐应力腐蚀断裂性优异的耐磨损钢板及其制造领域,能够解决耐磨损特性差、机械、装置发生故障、无法维持强度危险性等问题,达到优异耐应力腐蚀断裂性、寿命提高的效果

Active Publication Date: 2015-12-23
JFE STEEL CORP
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] If the wear resistance of the steel material is poor, it will not only cause failure of machinery and equipment, but also risk maintaining the strength of the structure, so frequent repairs and replacements of worn parts are unavoidable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Abrasion-resistant steel plate excellent in stress corrosion cracking resistance and manufacturing method thereof
  • Abrasion-resistant steel plate excellent in stress corrosion cracking resistance and manufacturing method thereof
  • Abrasion-resistant steel plate excellent in stress corrosion cracking resistance and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0104] Prepare steel slabs (steelslab) with various composition shown in Table 1-1 to Table 1-4 by using a converter-ladle refining-continuous casting method, and heat it to 950 to 1250°C After that, hot rolling is performed, and some steel plates are subjected to accelerated cooling immediately after rolling, and other steel plates are subjected to air cooling after rolling. Furthermore, some steel plates are subjected to accelerated cooling and tempering after reheating.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

Provided is an abrasion resistant steel plate or steel sheet suitable for use in construction machines, industrial machines, and the like and a method for manufacturing the same. In particular, a steel plate or steel sheet excellent in resistance to stress corrosion cracking has a composition containing 0.20% to 0.30% C, 0.05% to 1.0% Si, 0.40% to 1.20% Mn, P, S, 0.1% or less Al, 0.01% or less N, and 0.0003% to 0.0030% B on a mass basis, the composition further containing one or more of Cr, Mo, and W, the composition further containing one or more of Nb, Ti, Cu, Ni, V, an REM, Ca, and Mg as required, the remainder being Fe and inevitable impurities. DI* due to contained components is 45 or more. A microstructure has a base phase or main phase that is tempered martensite. Cementite having a grain size of 0.05 µm or less in terms of equivalent circle diameter is present in the steel plate or steel sheet at 2 x 10 6 grains / mm 2 or more. A semi-finished product having the above steel composition is heated, hot rolling is performed, air cooling is performed, reheating is performed, and accelerated cooling is then performed or accelerated cooling is performed immediately after hot rolling.

Description

technical field [0001] The present invention relates to an abrasion resistant steel plate (abrasion resistant steel plate or steel sheet) with a plate thickness of 4 mm or more suitable for construction machines, industrial machines, shipbuilding, steel pipes, civil engineering, buildings, etc. It relates to a steel plate excellent in resistance of stress corrosion cracking (resistance of stress corrosion crack). Background technique [0002] When hot-rolled steel sheets are used in iron and steel structures, machines, devices, etc. of construction machinery, shipbuilding, steel pipes, civil engineering, and buildings, the abrasion resistance property of the steel sheet may be required. Abrasion is a phenomenon in which the surface of steel is scraped off due to continuous contact between steel materials or different types of materials such as sand, rocks, etc. [0003] If the wear resistance of steel materials is poor, not only will it cause failure of machinery and equipm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/00C21D8/02C22C38/32C22C38/54
CPCC21D1/25C21D8/0263C21D8/0426C21D8/0463C21D8/0473C21D2211/008C22C38/00C22C38/001C22C38/002C22C38/02C22C38/04C22C38/06C22C38/12C22C38/18C22C38/20C22C38/22C22C38/24C22C38/26C22C38/28C22C38/40C22C38/50C22C38/54
Inventor 植田圭治石川信行
Owner JFE STEEL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products