High-temperature resistant oil well rubber sealing ring material and preparation method thereof
A technology of rubber sealing ring and high temperature resistance, applied in the field of rubber materials, can solve the problems of reduced service life, aging and loss of rubber sealing packing, etc., and achieve poor compatibility and adhesion, good high temperature resistance, and reduced raw material costs Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0041] Example 1:
[0042] Inner glue:
[0043]
[0044] middle layer:
[0045]
[0046] Outer glue:
[0047]
[0048] (1) According to the formula of Example 1, weigh the raw materials of the inner and outer layer rubber and the middle layer, except for the high-strength woven fabric, and mix them with an open mill or internal mixer, and then filter the mixed rubber powder separately To remove impurities and obtain pre-rubber powder;
[0049] (2) Pass the pre-rubber powder obtained in step (1) through a cold-feed compound extruder (SH-36, Nanjing Jieya Extrusion Equipment Co., Ltd., the temperature of the extruder is set between 80-100°C) Extrude the inner and outer layers and the middle layer of glue. When extruding, control the thickness of the glue layer to 10mm, and cut it to the specified size as needed;
[0050] (3) In the order of "rubber-woven fabric-rubber-woven fabric-rubber", add the rubber material of the inner layer, middle layer, outer layer and woven cloth cut in step (...
Example Embodiment
[0053] Example 2
[0054] Inner glue:
[0055]
[0056] middle layer:
[0057]
[0058] Outer glue:
[0059]
[0060] The preparation method of this embodiment is similar to that of embodiment 1. During the preparation process: the thickness of the extruded rubber layer is 8mm, the thickness of the added woven cloth is 0.4mm, the inner and outer layers are both 4-layered, and the middle layer is 5-layer structure, curing time is 25min, curing temperature is 165℃.
Example Embodiment
[0061] Example 3
[0062] Inner glue:
[0063]
[0064] middle layer:
[0065]
[0066] Outer glue:
[0067]
[0068] The preparation method of this embodiment is similar to that of embodiment 1. During the preparation process: the thickness of the extruded rubber layer is 4mm, the thickness of the added woven cloth is 0.1mm, the inner and outer layers are both set to have a 7-layer structure, and the middle layer is 5-layer structure, curing time is 20min, curing temperature is 150℃.
[0069] The performance tests of the finished products prepared in the above 3 examples are as follows:
[0070]
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap