Method for modified silicon iron boron soft magnetic powder core with magnetic conductivity of 90

A soft magnetic powder core and iron silicon boron technology is applied in the field of preparation of modified iron silicon boron soft magnetic powder core to achieve the effects of reducing noise, improving high-frequency characteristics and high-frequency magnetic permeability

Active Publication Date: 2014-01-08
QINGDAO YUNLU ADVANCED MATERIALS TECH CO LTD
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to solve the above problems, the purpose of the present invention is to provide a method for preparing a modified iron-silicon-boron soft magnetic powder core with a magnetic permeability of 90, which improves the iron-silicon-boron Noise defect of soft magnetic powder core and improve its high frequency characteristics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The preparation method of the modified FeSiB soft magnetic powder core provided in this embodiment includes the following steps,

[0027] Step 1, embrittlement treatment: heat-treat the iron-silicon-boron amorphous metal strip at 300°C for 2 hours to make it embrittled and easily crushed;

[0028] Step 2, crushing: crushing the brittle amorphous metal strip to obtain amorphous metal powder;

[0029] Step 3, sieving and proportioning: sieve the amorphous metal powder, and then mix it into the first powder with a weight content of 50% passing through -170~+200 mesh, and the weight content of 20% passing through- Powder granules composed of the second powder of 200~+270 mesh and the third powder passing through -270~+325 mesh with a weight content of 30%;

[0030] Step 4, passivation treatment and insulation coating: Pour the proportioned amorphous powder particles into the mixer, stir and mix evenly, then add phosphoric acid solution for passivation effect, the amoun...

Embodiment 2

[0054] The preparation method of the modified FeSiB soft magnetic powder core provided in this embodiment includes the following steps,

[0055] Step 1, embrittlement treatment: heat-treat the iron-silicon-boron amorphous metal strip at 300°C for 2 hours to make it embrittled and easily crushed;

[0056] Step 2, crushing: crushing the brittle amorphous metal strip to obtain amorphous metal powder;

[0057] Step 3, sieving and proportioning: sieving the amorphous metal powder, and then mixing it into the first powder with a weight content of 20-70% passing through -170-+200 mesh, and a weight content of 10-40 % of the second powder passing through the mesh of -200~+270 and the powder particles composed of the third powder passing through the mesh of -270~+325 with a weight content of 20~40%;

[0058] Step 4, passivation treatment and insulation coating: Pour the proportioned amorphous powder particles into the mixer, stir and mix evenly, then add phosphoric acid solution f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of metal soft magnetic material manufacturing, and particularly relates to a method for manufacturing a modified silicon iron boron soft magnetic powder core with magnetic conductivity of 90. The method comprises the first step of embrittlement treatment, the second step of crushing, the third step of screening and matching, the fourth step of passivating treatment and insulation covering, the fifth step of modifying agent adding, the sixth step of compression moulding and the seventh step of annealing treatment and spraying. According to the method, the noise defect of the silicon iron boron soft magnetic powder core can be overcome, and the high-frequency performance of the silicon iron boron soft magnetic powder core can be improved.

Description

technical field [0001] The invention belongs to the field of metal soft magnetic material manufacturing, and in particular relates to a method for preparing a modified iron-silicon-boron soft magnetic powder core with a magnetic permeability of 90. Background technique [0002] Since Professor Duwez in the United States invented the rapid quenching process to prepare amorphous alloys in 1960, due to its unique structure, efficient preparation process, excellent material properties and broad application prospects, it has been favored by material scientists and the industry. of special attention. Amorphous magnetic powder core is a new type of composite electronic material, mainly used in switching power supply cores, common-mode inductors, high-frequency inverters and zero-sequence transformers. [0003] At present, the magnetic powder core products mainly include iron silicon boron magnetic powder cores, sendust magnetic powder cores, iron nickel magnetic powder cores, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01F41/02H01F1/147H01F1/24B22F9/04B22F1/02B22F3/02
Inventor 纪杰江志滨王亚娜李维强姜海滨
Owner QINGDAO YUNLU ADVANCED MATERIALS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap