Gapless atom cold-rolled hot-galvanized steel plate and production method thereof

A technology of hot-dip galvanized steel sheet without interstitial atoms, which is applied in the field of iron-based alloys, can solve problems such as product performance not meeting requirements, and achieve the effect of reducing production costs

Active Publication Date: 2014-01-15
SHANGHAI MEISHAN IRON & STEEL CO LTD
View PDF4 Cites 33 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a kind of interstitial-free cold-rolled hot-dip galvanized steel sheet and its production method, which mainly solves the problem that the performance of the p

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Gapless atom cold-rolled hot-galvanized steel plate and production method thereof
  • Gapless atom cold-rolled hot-galvanized steel plate and production method thereof
  • Gapless atom cold-rolled hot-galvanized steel plate and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0039] The present invention will be further described below in conjunction with Examples 1-4, as shown in Table 1-Table 4.

[0040]Table 1 The present invention (% by weight), the balance is Fe and unavoidable impurities.

[0041] the element

C

Si

mn

Ti

N

P

S

this invention

0.0005-0.0028

≤0.03

0.08-020

0.02-0.065

≤0.0030

≤0.015

≤0.010

Example 1

0.0007

0.011

0.19

0.024

0.0030

0.011

0.010

Example 2

0.0025

0.007

0.14

0.047

0.0021

0.012

0.009

Example 3

0.0012

0.005

0.09

0.060

0.0016

0.008

0.008

Example 4

0.0014

0.006

0.15

0.048

0.0019

0.012

0.008

[0042] Through converter smelting and RH furnace vacuum decarburization, the continuous casting slab meeting the required chemical composition...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a gapless atom cold-rolled hot galvanized steel plate and a production method thereof, which belongs to the technical field of iron-base alloys and solves the technical problem that the product performance can not reach the standard when a horizontal continuous annealing furnace is adopted for annealing to produce the gapless atom hot-galvanized steel plate in the prior art. The technical scheme is as follows: the gapless atom cold-rolled hot galvanized steel plate comprises the following chemical components in percentage by weight: 0.0005%-0.0028% of C, at most 0.03% of Si, 0.08%-0.20% of Mn, 0.02%-0.065% of Ti, at most 0.0030% of N, at most 0.015% of P, at most 0.010% of S, and the balance of Fe and inevitable impurity elements. The microscopic structure grain fineness of the cold-rolled steel plate is Grade I6.5-I8.0, the yield strength is 165-200 MPa, the tensile strength is 270-330 MPa, the percentage elongation after fracture A80mm is 38-44%, and the plastic strain ratio r is greater than or equal to 1.9. The method lowers the production cost of the gapless atom cold-rolled hot-galvanized steel plate. The product is mainly used for home appliance products, hardware structures and the like.

Description

technical field [0001] The invention relates to a cold-rolled hot-dip galvanized steel sheet without interstitial atoms and a production method thereof, belonging to the technical field of iron-based alloys. Background technique [0002] Interstitial-free steel is also called IF steel (short for Interstitial-Free Steel). Because it has no interstitial atoms, it has excellent deep drawing performance and non-aging performance, especially hot-dip galvanized steel sheets without interstitial atoms, which have more excellent stamping performance after cold rolling and annealing above the recrystallization temperature. There are two existing technologies for producing hot-dip galvanized IF steel products, one is to go through the bell annealing process and then go through hot-dip after cleaning, and the other is to go through the continuous annealing process and then directly hot-dip. Compared with the bell-type annealing process, direct hot-dip galvanizing after continuous anne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/14C21D8/02
Inventor 丁志龙张伟超
Owner SHANGHAI MEISHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap