Ceramic coating with marine organism corrosion resistance as well as preparation method thereof

A technology of ceramic coating and bio-corrosion, which is applied in the field of ceramic production, can solve problems such as unapplied applications, and achieve the effect of expanding application and improving anti-corrosion performance of marine organisms

Active Publication Date: 2014-01-29
嘉善县临沪新城实业有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, in China, there is still no patent application for ceramic coatings that resist marine biocorrosion.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A kind of anti-corrosion ceramic coating of marine organisms, the parts by weight of each component are:

[0017] 20 parts of magnesium oxide, 60 parts of aluminum oxide, 10 parts of silicon dioxide, and 10 parts of zinc oxide.

[0018] Its preparation method comprises the following steps:

[0019] Weigh 20 parts of magnesium oxide, 60 parts of aluminum oxide, 10 parts of silicon dioxide, and 10 parts of zinc oxide, burn magnesium oxide and aluminum oxide at 1100°C for 70 minutes, and burn silicon dioxide and zinc oxide at 940°C for 30 minutes, take out Cool to room temperature to obtain a ceramic coating resistant to marine corrosion;

Embodiment 2

[0021] A kind of anti-corrosion ceramic coating of marine organisms, the parts by weight of each component are:

[0022] 25 parts of magnesium oxide, 55 parts of aluminum oxide, 10 parts of silicon dioxide, and 10 parts of zinc oxide.

[0023] Its preparation method comprises the following steps:

[0024] Weigh 25 parts of magnesium oxide, 55 parts of aluminum oxide, 10 parts of silicon dioxide, and 10 parts of zinc oxide, burn magnesium oxide and aluminum oxide at 1200°C for 80 minutes, and burn silicon dioxide and zinc oxide at 940°C for 40 minutes, take out Cool to room temperature to obtain a ceramic coating resistant to marine corrosion;

Embodiment 3

[0026] A kind of anti-corrosion ceramic coating of marine organisms, the parts by weight of each component are:

[0027] 25 parts of magnesium oxide, 60 parts of aluminum oxide, 5 parts of silicon dioxide, and 10 parts of zinc oxide.

[0028] Its preparation method comprises the following steps:

[0029] Weigh 25 parts of magnesium oxide, 60 parts of aluminum oxide, 5 parts of silicon dioxide, and 10 parts of zinc oxide, burn magnesium oxide and aluminum oxide at 1000°C for 70 minutes, and burn silicon dioxide and zinc oxide at 1000°C for 50 minutes, take out Cool to room temperature to obtain a ceramic coating resistant to marine corrosion;

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to ceramic coating with marine organism corrosion resistance as well as a preparation method therefore, belonging to the technical field of ceramics. The ceramic coating comprises the following components in parts by weight: 15-30 parts of magnesium oxide, 50-70 parts of aluminum oxide, 5-20 parts of silicon dioxide and 2-20 parts of zinc oxide. The preparation method comprises the following steps of: firing the components for 30 minutes-100 minutes at a high temperature of 800 DEG C-1500 DEG C; and taking out and cooling to the room temperature to obtain the ceramic coating with the marine organism corrosion resistance. The ceramic coating disclosed by the invention not only keeps original characteristics of wear resistance, high temperature resistance, oxidization resistance and the like of the ceramic coating; meanwhile, the aluminum oxide is added, so that the marine organism corrosion resistance of the coating is remarkably improved, and application of the ceramic coating on components of ships and warships is expanded.

Description

technical field [0001] The invention relates to a ceramic coating resistant to marine organism corrosion, in particular to a ceramic coating resistant to marine organism corrosion and a preparation method thereof, belonging to the technical field of ceramic production. Background technique [0002] With the development of maritime traffic, the proportion of ship repair and maintenance to the cost of navigation is gradually increasing. How to reduce the cost of ship repair and maintenance is one of the main problems faced by various shipping companies. Among all the ship repair work, the repair and maintenance of ship parts due to seawater corrosion is particularly prominent and accounts for the largest proportion of repair costs. Ships have been immersed in seawater for many years, and they are inevitably corroded by seawater and marine microorganisms, resulting in varying degrees of damage to parts and components. Therefore, it is very important to research and develop ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/10C04B35/622
Inventor 陈春水
Owner 嘉善县临沪新城实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products