Mixed cathode material for lithium ion batteries and preparation method thereof

A lithium-ion battery and positive electrode technology, which is applied in the direction of battery electrodes, circuits, electrical components, etc., can solve the problems of low consistency, cycle life, and limited safety improvement, and achieve the effect of long life

Active Publication Date: 2014-03-26
SUZHOU GCL ENERGY TECH DEV CO LTD
View PDF2 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The current method of use is mostly for battery manufacturers to purchase raw materials from cathode material manufacturers for simple mixing a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mixed cathode material for lithium ion batteries and preparation method thereof
  • Mixed cathode material for lithium ion batteries and preparation method thereof
  • Mixed cathode material for lithium ion batteries and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0049] Example 1

[0050] 1. Raw material A is selected as LiMn 1.9 Al 0.05 Co 0.05 O 3.98 F 0.02 , the average particle size is 10μm, and the specific surface area is 0.35m 2 / g, raw material B is LiNi 0.333 Co 0.329 Mn 0.333 Mg 0.004 O 2 , the average particle size is 10μm, the specific surface area is 0.30m 2 / g;

[0051] 2. Put 50wt% of raw material A and 50wt% of raw material B into a polyethylene container with a stirrer, add deionized water equivalent to 3 times the weight of the powder, start the stirrer, and stir at 500rpm for 20min.

[0052] 3. Liquid coating agents E and F were added dropwise to the polyethylene container filled with materials and dispersants through two peristaltic pumps, where E was a 0.2 mol / l concentration of lithium hydroxide aqueous solution, and F was a 0.2 mol / l concentration aqueous solution of aluminum nitrate. Control the dripping amount of the aluminum nitrate aqueous solution so that the aluminum element in the dripping ...

Example Embodiment

[0054] Example 2

[0055] 1. Raw material A is selected as LiMn 1.9 Al 0.05 Mg 0.05 O 3.98 F 0.02 , the average particle size is 10μm, and the specific surface area is 0.35m 2 / g, raw material B is LiNi 0.333 Co 0.329 Mn 0.333 Ti 0.002 Mg 0.002 O 2 , the average particle size is 10μm, the specific surface area is 0.30m 2 / g;

[0056] 2. Put 50wt% of raw material A and 50wt% of raw material B into a polyethylene container with a stirrer, add deionized water equivalent to 3 times the weight of the powder, start the stirrer, and stir at 500rpm for 20min.

[0057] 3. Liquid coating agents E and F were added dropwise to the polyethylene container filled with materials and dispersants through two peristaltic pumps, wherein E was 0.2 mol / l concentration of ammonium phosphate aqueous solution, and F was 0.2 mol / l concentration of ammonium phosphate solution. Aqueous solution of aluminum nitrate. Control the dripping amount of the aluminum nitrate aqueous solution so t...

Example Embodiment

[0059] Example 3

[0060] 1. Raw material A is selected as LiMn 1.9 Al 0.05 Mg 0.05 O 3.98 F 0.02 , the average particle size is 10μm, and the specific surface area is 0.35m 2 / g, raw material B is LiNi 0.333 Co 0.329 Mn 0.333 Ti 0.002 Mg 0.002 O 2 , the average particle size is 10μm, the specific surface area is 0.30m 2 / g, raw material C-site LiNi 0.5 Co 0.196 Mn 0.3 Al 0.004 O 2 , the average particle size is 10μm, and the specific surface area is 0.35m 2 / g;

[0061] 2. Put 50wt% of raw material A, 30wt% of raw material B, and 20wt% of raw material C into a polyethylene container with a stirrer, add deionized water equivalent to 3 times the weight of the powder, start the stirrer, and stir at 500rpm for 20min .

[0062] 3. Liquid coating agents E and F were added dropwise to the polyethylene container filled with materials and dispersants through two peristaltic pumps, where E was a 0.2 mol / l concentration of lithium hydroxide aqueous solution, and F ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of batteries, and in particular relates to a long-life, high-energy density and low-cost mixed cathode material for lithium ion secondary batteries and a preparation method thereof. The mixed cathode material for the lithium ion batteries, provided by the invention, comprises the following raw components in percentage by weight: 20-60% of doped lithium-manganese spinel composite oxide and 40-80% of doped lithium-nickel-cobalt-manganese composite oxide. According to the mixed cathode material for the lithium ion batteries, provided by the invention, proper doping is carried out on lithium-manganese spinel to ensure that the lattice imperfection can be effectively reduced, the crystal structure is stabilized, the lattice distortion is restrained, the manganese dissolution is reduced, the cycle life is prolonged, the large current charge-discharge property and safety performance can be improved so as to satisfy the important requirements on the lithium ion batteries for EV (Electric Vehicles) and HEV (Hybrid Electric Vehicles); for the lithium-nickel-cobalt-manganese composite oxide of a layered structure, the doping has the same effect and the cycle performance, the rate performance and the safety performance can be better improved.

Description

technical field [0001] The invention relates to the field of batteries, in particular to a hybrid positive electrode material of a lithium-ion secondary battery with high service life, high energy density and lower cost and a preparation method thereof. Background technique [0002] With the rising energy prices and increasing environmental pressure, the automotive industry's demand for new energy power technologies has grown rapidly. Lithium-ion batteries are now regarded as a new power source by more and more companies and researchers, which urgently requires the development of lithium-ion battery cathode materials with high safety, high energy density, high power, long cycle, high environmental protection and low price . [0003] Based on safety and cost considerations, lithium manganese spinel cathode material is now considered to be an advantageous cathode material for lithium-ion batteries for power use. However, during the charging and discharging process, especiall...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M4/48H01M4/62
CPCH01M4/505H01M4/525Y02E60/10
Inventor 卢永强孙化雨
Owner SUZHOU GCL ENERGY TECH DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap