A sensitive, reliable, fast and stable multi-element simultaneous detection method for iron ore

A simultaneous detection and iron ore technology, applied in the preparation of test samples, thermal excitation analysis, material excitation analysis, etc., can solve the problem of accuracy of detection results, unsatisfactory reproducibility, narrow detection range of atomic absorption spectrometry, The analysis results have a relatively large impact, and achieve the effects of reducing volatile emissions and impurity pollution, high sex-to-background ratio, and rich spectral lines

Active Publication Date: 2016-02-10
WUKUN STEEL
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the commonly used iron ore element detection methods mainly include photometry, atomic absorption spectrometry and X-ray fluorescence spectrometry, among which photometry is complicated to operate, requires a lot of reagents, and the stability of the measurement results is slightly poor; the detection range of atomic absorption spectrometry is narrow. , it is not suitable for large-scale multi-element detection and analysis; although X-ray fluorescence spectroscopy overcomes the shortcomings of long analysis period and time-consuming and labor-intensive methods, due to the use of tablet method for sample preparation, the analysis results are greatly affected by the matrix, resulting in inaccurate detection results unsatisfactory reproducibility

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A sensitive, reliable, fast and stable multi-element simultaneous detection method for iron ore
  • A sensitive, reliable, fast and stable multi-element simultaneous detection method for iron ore
  • A sensitive, reliable, fast and stable multi-element simultaneous detection method for iron ore

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] ——Detection of arsenic iron ore YSBC14721-98

[0044] A. Sample preparation: put 0.15g of the powder of arsenic-containing iron ore YSBC14721-98 to be tested into a polytetrafluoroethylene beaker, add a mixed acid of hydrochloric acid and nitric acid with a volume ratio of 4:1 according to the dosage of 225ml / g, and dissolve the sample Dissolve to obtain solution a; add hydrofluoric acid to solution a according to the dosage of 9ml / ml, heat at 225°C for 12min to obtain solution b; add perchloric acid to solution b according to the dosage of 5ml / ml , heated at 225°C until smoking, 1ml of the solution remained, and the solution c was obtained after cooling; according to the dosage of 12ml / ml, dilute hydrochloric acid mixed with hydrochloric acid and water at a volume ratio of 1:1 was added to the solution c to dissolve After filtering, dilute the filtrate with water to 0.001g / ml to obtain the test solution d.

[0045] B. Calibration: Set the working conditions of the ind...

Embodiment 2

[0056] ——Detection of vanadium-titanium magnetite concentrate YSBC19717-2005

[0057] A, sample preparation: 0.1g of the powder of the vanadium-titanium magnetite concentrate YSBC19717-2005 to be tested is placed in a polytetrafluoroethylene beaker, and a mixed acid of hydrochloric acid and nitric acid with a volume ratio of 5:1 is added according to the consumption of 200ml / g. Dissolve the sample to obtain solution a; add hydrofluoric acid to solution a according to the dosage of 7ml / ml, heat at 250°C for 10 minutes to obtain solution b; add perchloric acid to solution b according to the dosage of 4ml / ml Acid, heated at 250°C until smoking, 0.8ml of solution remains, and after cooling, solution c is obtained; according to the dosage of 10ml / ml, add dilute hydrochloric acid mixed with hydrochloric acid and water at a volume ratio of 1:1.2 to solution c , filtered after dissolving, and dilute the filtrate to 0.0008g / ml with water to obtain the test solution d.

[0058] B. Cali...

Embodiment 3

[0069] ——Detection of iron ore YSBC13710-95

[0070] A. Sample preparation: put 0.2g of the powder of iron ore YSBC13710-95 to be tested into a polytetrafluoroethylene beaker, add a mixed acid of hydrochloric acid and nitric acid with a volume ratio of 3:1 according to the dosage of 250ml / g, and dissolve the sample , to obtain the solution a; add hydrofluoric acid to the solution a according to the dosage of 12ml / ml, and heat at 200°C for 15min to obtain the solution b; add perchloric acid to the solution b according to the dosage of 6ml / ml, Heating at 200°C until smoking, 1.2ml of the solution remains, and after cooling, the solution c is obtained; add dilute hydrochloric acid mixed with hydrochloric acid and water at a volume ratio of 1:0.8 to the solution c according to the dosage of 15ml / ml, and dissolve After filtering, dilute the filtrate with water to 0.0012g / ml to obtain the test solution d.

[0071] B. Calibration: Set the working conditions of the inductively couple...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a sensitive, reliable, fast and stable iron ore multi-element synchronous detection method, which belongs to the technical field of metallurgical material testing and analysis. Add 3~5:1 mixed acid of hydrochloric acid and nitric acid at 200~250ml / g to 0.1~0.2g iron ore powder to dissolve it; Heat for 10~15min; add perchloric acid in an amount of 4~6ml / ml, heat at 200~250℃ until the solution remains 0.8~1.2ml; add dilute hydrochloric acid in an amount of 10~15ml / ml, dissolve, filter, and dilute to 0.0008~0.0012g / ml was the solution to be tested. Prepare standard solutions with different concentration gradients for each element, select the analysis lines and working conditions of each element in the inductively coupled plasma emission spectrum; measure the emission intensity of each element analysis line to draw a standard curve; detect the emission intensity corresponding to each element , according to the standard curve to determine the content of each element. The method is sensitive, reliable, fast and stable, can provide analysis data for the smelting production process in time, improves production efficiency and equipment utilization rate, and has high application and promotion value.

Description

technical field [0001] The invention belongs to the technical field of metallurgical material testing and analysis, and in particular relates to a sensitive, reliable, fast and stable iron ore multi-element synchronous detection method. Background technique [0002] In order to effectively control the composition of the charge during iron ore smelting, quantitative analysis of the elemental composition in iron ore is required. At present, the commonly used iron ore element detection methods mainly include photometry, atomic absorption spectrometry and X-ray fluorescence spectrometry, etc. Among them, photometry is complicated to operate, requires a lot of reagents, and the stability of the measurement results is slightly poor; atomic absorption spectrometry has a narrow detection range. , it is not suitable for large-scale multi-element detection and analysis; although X-ray fluorescence spectroscopy overcomes the shortcomings of long analysis period and time-consuming and l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N21/71G01N1/28
Inventor 李竞春赵征宇马林泽李洁严海陈燕燕万林白乘舟
Owner WUKUN STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com