High-property long glass fiber reinforced nylon 66 composite material and preparation process thereof

A preparation process and composite material technology, applied in the field of high-performance long glass fiber reinforced nylon 66 composite material and its preparation, can solve the problems of limited fiber reinforced modification effect and small fiber length, and achieve a wide range of applications and reduced costs. Effect

Inactive Publication Date: 2014-04-09
MIANYANG PENGYANG POLYMER MATERIAL
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the mixing of these materials adopts the process of twin-screw melt mixing. The fibers are broken in a large number in the screw, and the length of the fibers retained in the product after molding is very small, so the reinforcement and modification effect of the fibers is very limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] High-performance long glass fiber reinforced nylon 66 composite material and its preparation process, using the following raw materials in mass percentage:

[0024] Low-viscosity nylon 66: 50% to 80%;

[0025] Special long glass fiber: 20% to 50%;

[0026] Compatibilizer: 5% to 8%;

[0027] Special nylon 66 rheology modifier: 0.3% to 1.0%;

[0028] Silicone powder: 0.3% to 0.5%;

[0029] Calcium stearate: 0.3% to 0.5%.

[0030] According to the specific requirements of different customers, the following raw materials with different mass percentages are used:

[0031] 1. The mechanical performance requirements of the material are only 10% to 20% higher than that of ordinary reinforced nylon 66, and the following raw materials are used in mass percentage:

[0032] Low viscosity nylon 66: 75%;

[0033] Special long glass fiber: 20%;

[0034] Compatibilizer: 5%;

[0035] Special nylon 66 rheology modifier: 0.3%;

[0036] Silicone powder: 0.5%;

[0037] Calcium ste...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a high-property long glass fiber reinforced nylon 66 composite material and a preparation process thereof. The high-property long glass fiber reinforced nylon 66 composite material is prepared from the following raw materials by mass percent: 66.50%-80% of low-viscosity nylon, 20%-50% of special long glass fibers, 5%-8% of a compatilizer, 0.3%-1.0% of a special nylon 66 rheology modifier, 0.3%-0.5% of silicone powder and 0.3%-0.5% of calcium stearate. The preparation process comprises the main steps: manufacturing a special die and a special drying box; selecting liquid glue to bind glass fibers; weighing the nylon 66, the special nylon 66 rheology modifier, the silicone powder and calcium stearate; uniformly mixing; realizing a molten state under the effect of a single-screw extruder; feeding the molten mixture into a cavity of a die special for long glass production at a constant speed; immersing together with the long glass fibers which are dried and pulled into the cavity of the die; pulling out the immersed glass fibers under the traction of a tractor at the regular speed; feeding into a special granulator for granulation.

Description

technical field [0001] The invention relates to the field of plastic modified materials, and specifically discloses a high-performance long glass fiber reinforced nylon 66 composite material and a preparation process thereof. Background technique [0002] Short fiber-reinforced thermoplastic composites, or fiber-reinforced materials of the traditional concept, have greatly improved mechanical properties compared with unreinforced materials, and at the same time have the dual advantages of reducing material costs, so they are used for reinforcement modification of most materials. Such as polypropylene, nylon, polyphenylene sulfide, polyoxymethylene, PET, PBT, etc. However, the mixing of these materials adopts the process of twin-screw melt mixing, and the fibers are broken in a large number in the screw, and the length of the fibers retained in the product after molding is very small, and the effect of fiber reinforcement and modification is very limited. How to increase the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/06C08L83/04C08K7/14C08K5/098
CPCC08L77/06B29B9/06B29C48/92B29C2948/9258B29C2948/92704C08L83/04C08K7/14C08K5/098
Inventor 魏闻刘昭
Owner MIANYANG PENGYANG POLYMER MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap