Method for improving pop strength of paper sheet and paper sheet manufactured through method

A technology of bursting strength and paper, applied in the field of paper to improve the bursting strength of paper, can solve the problems of increasing dosage, increased input cost, inability to achieve high bursting strength, increased input cost, and improved bursting strength.

Active Publication Date: 2014-04-23
GOLD EAST PAPER JIANGSU
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the limitation of refining capacity, the maximum addition amount of long fiber cannot be increased more (under normal conditions, the maximum feeding capacity of long fiber refining line can only account for 30% of the total pulp)
The most direct way to increase the refining capacity of the pulp line is to increase the number of disc refiners, whic

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0027] Example 1

[0028] In the long fiber refining line and the short fiber refining line, the long fiber pulp accounts for 56% of the total slurry, and the remaining is short fiber pulp; among them, the long fiber pulp added to the short fiber refining line accounts for the total slurry Of 25%. The pulp line is provided with two refiners in series, and the power ratio of the two refiners along the flow direction of the slurry is 45:55. After refining, the freeness of the long fiber pulp in the long fiber refining line reached 461ml, and the freeness of the mixed pulp of long and short fibers in the short fiber refining line reached 403ml. Under the premise that the speed ratio of the slurry to the network is greater than 1, reduce the speed of the slurry supply pump.

[0029] The grammage of the paper prepared in Example 1 was 80 g, the burst strength reached 346 kPa, and the burst strength was much higher than the national standard (over the target burst strength of 320 kPa)....

Example Embodiment

[0031] Example 2

[0032] In the long fiber refining line and the short fiber refining line, the long fiber pulp accounts for 58% of the total slurry, and the remainder is the short fiber pulp; the long fiber pulp added to the short fiber refining line accounts for the total slurry Of 28%. The pulp line is provided with two refiners in series, and the power ratio of the two refiners along the flow direction of the slurry is 45:55. After refining, the freeness of long fiber pulp in the long fiber refining line reached 447ml, and the freeness of the mixed pulp of long and short fibers in the short fiber refining line reached 419ml. Under the premise that the speed ratio of the slurry to the network is greater than 1, reduce the speed of the slurry supply pump.

[0033] The grammage of the paper prepared in Example 2 is 120g, the burst strength reaches 407kPa, and the burst strength is much higher than the national standard (over the target burst strength of 380kPa).

Example Embodiment

[0034] Example 3

[0035] In the long fiber refining line and the short fiber refining line, the long fiber pulp accounts for 59% of the total slurry, and the remainder is the short fiber pulp; the long fiber pulp added to the short fiber refining line accounts for the total slurry Of 29%. When three refiners connected in series are arranged on the pulp line, the power ratio of the three refiners along the flow direction of the slurry is 25:35:40. After refining, the freeness of the long fiber pulp in the long fiber refining line reached 461ml, and the freeness of the mixed pulp of long fiber and short fiber in the short fiber refining line reached 434ml. Under the premise that the speed ratio of the slurry to the network is greater than 1, reduce the speed of the slurry supply pump.

[0036] The grammage of the paper prepared in Example 3 is 100g, the burst strength reaches 352kPa, and the burst strength is much higher than the national standard (exceeding the target burst stren...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Freenessaaaaaaaaaa
Bursting strengthaaaaaaaaaa
Gram weightaaaaaaaaaa
Login to view more

Abstract

The invention provides a method for improving the pop strength of a paper sheet. The method includes the following steps that long fibers and short fibers are selected for use; a long fiber pulping line and a short fiber pulping line are adopted, the short fibers and long fibers are added in the short fiber pulping line, and only the long fibers are added in the long fiber pulping line; the added long fibber pulp accounts for the total amount of pulp by 55-60% in the long fiber pulping line and the short fiber pulping line, the balance is the short fiber pulp, and the long fiber pulp added in the short fiber pulping line accounts for the total amount of pulp by 25-30%; at least two pulping machines are arranged in series in each pulping line, and in the flowing direction of the pulp, power distribution proportions of all the pulping machines are set from low to high; on the premise that the ratio of net touch speed of the pulp to moving speed of a formation net is controlled to be larger than one, rotation speed of a pulp supplying pump is reduced. The invention further provides the paper sheet manufactured through the method. The method can achieve the purpose of improving the pop strength without increasing investment cost.

Description

technical field [0001] The invention relates to a method for increasing the bursting strength of paper and the paper prepared by the method. Background technique [0002] Bursting strength is an important index to measure the strength of paper. Paper with high bursting strength is widely used in the production of paper bags, envelopes, record sleeves, files and sandpaper. The improvement of bursting strength depends to a large extent on the strength of raw pulp, beating process and fiber distribution. [0003] The burst index of softwood pulp (long fiber) is much higher than that of hardwood pulp (short fiber). The burst index of long fiber is 6-8kgf / cm, and that of short fiber is 2.5-4kgf / cm. Therefore, using a large amount of long fibers can effectively improve the bursting strength of paper sheets. However, according to the production capacity of the paper machine, the relevant refining lines designed for each large-scale cultural paper machine are divided into long-fi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21D1/20D21H15/10
Inventor 翟凤卫李云胜刘龙坤朱成刚
Owner GOLD EAST PAPER JIANGSU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap