Preparation method of silicon carbide abrasion-resistant fire-resistant furnace body lining brick
A refractory furnace and silicon carbide technology, applied in the field of furnace lining bricks, can solve the problems of short service life of clay-bonded furnace lining bricks, avoid sticking to the furnace wall, inhibit oxidation and decomposition, enhance compactness and wear resistance Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0021] Embodiment 1: A kind of preparation method of silicon carbide wear-resistant refractory furnace body lining brick, carry out according to the following steps:
[0022] a. Ingredients:
[0023] In parts by weight, the main ingredient proportioning is as follows:
[0024] 30 parts of waste high-voltage electric ceramics with a particle size of 1mm-3mm; 20 parts of fused brown corundum with a particle size of less than 1mm; 5 parts of high-alumina bauxite clinker with a particle size of ≥300 mesh; 8 parts of SiC with a particle size of 12 parts of 300 mesh SiC; 10 parts of SiC with a particle size of 5 μm; 15 parts of high-quality clay fine powder with a particle size ≥ 300 mesh; a total of 100 parts.
[0025] Combined sintering aid: phosphate solution, the total amount added accounts for 5% of the total weight of the above main ingredients;
[0026] Retarder: citric acid, accounting for 0.02% of the total weight of the above main ingredients;
[0027] Antioxidant: met...
Embodiment 2
[0032] Embodiment 2: A kind of preparation method of silicon carbide wear-resistant refractory furnace body lining brick, carry out according to the following steps:
[0033] a. Ingredients:
[0034] In parts by weight, the main ingredient proportioning is as follows:
[0035] 40 parts of waste high voltage electric porcelain with a particle size of 1mm-3mm; 10 parts of fused brown corundum with a particle size of less than 1mm; 7 parts of high-alumina bauxite clinker with a particle size of ≥300 mesh; 3 parts of SiC with a particle size of less than 1mm; 15 parts of 300 mesh SiC; 5 parts of SiC with a particle size of 5 μm; 20 parts of high-quality clay fine powder with a particle size of ≥300 mesh; a total of 100 parts.
[0036] Combined sintering aid: phosphate solution, the total amount added accounts for 7% of the total weight of the above main ingredients;
[0037] Retarder: citric acid, accounting for 0.06% of the above-mentioned main ingredient gross weight;
[003...
Embodiment 3
[0044] Embodiment 3: A kind of preparation method of silicon carbide wear-resistant refractory furnace body lining brick, carry out according to the following steps:
[0045] a. Ingredients:
[0046] In parts by weight, the main ingredient proportioning is as follows:
[0047] 35 parts of high-alumina bauxite clinker with a particle size of 1mm-3mm; 15 parts of fused brown corundum with a particle size of less than 1mm; 10 parts of high-alumina bauxite clinker with a particle size of ≥300 mesh; 5 parts of SiC with a particle size of less than 1mm; 12 parts of SiC with a particle size ≥ 300 mesh; 8 parts of SiC with a particle size ≥ 300 mesh; 15 parts of high-quality clay fine powder with a particle size ≥ 300 mesh; a total of 100 parts.
[0048] Combined sintering aid: 42.5% phosphoric acid solution, the total amount added accounts for 8% of the total weight of the above main ingredients;
[0049] Retarder: oxalic acid, accounting for 0.04% of the total weight of the above...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap