Gap filler

A technology of caulking agent and antifungal agent, which is applied in the field of caulking agent for tile paving, which can solve problems such as easy cracking, low adhesion of caulking agent, and tile bursting, so as to achieve improved lubrication and good water resistance , cost reduction effect

Inactive Publication Date: 2014-05-21
QINGDAO BAOLIKANG NEW MATERIALS
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The laying of ceramic tiles has become a common decoration in daily life. From home to hotels and other public places, from the ground to the wall, the decorative effect brought by ceramic tiles cannot be underestimated. However, in the process of laying and laying, bricks and bricks The joints between the blocks need to be specially treated. At present, the commonly used joint sealant is cement mortar, which has low adhesion and is prone to cracking after curing, thus absorbing water. If it encounters thermal expansion and contraction, it will Cause the tiles to burst, or too much water seeps in and the adhesion between the tiles and the wall is not strong enough to fall off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Example 1, this example discloses a joint filler, including the following components by weight: 50 parts of quartz sand, 30 parts of Portland cement, 8 parts of antioxidant, 2 parts of limestone, and 2 parts of silicone leveling agent , 2 parts of antifungal agent, 6 parts of inorganic aluminum salt water repellent.

[0011] The caulking agent disclosed in this embodiment has good water resistance, mildew and oxidation resistance, easy and safe construction, and is a good tile paving caulking agent.

Embodiment 2

[0012] Embodiment 2, this embodiment discloses a joint filler, including the following components by weight: 60 parts of quartz sand, 20 parts of Portland cement, 6 parts of antioxidant, 3 parts of limestone, and 2 parts of silicone leveling agent , 2 parts of antifungal agent, 7 parts of inorganic aluminum salt water repellent.

[0013] The caulking agent disclosed in this embodiment has good water resistance, mildew and oxidation resistance, easy and safe construction, and is a good tile paving caulking agent.

Embodiment 3

[0014] Embodiment 3, this embodiment discloses a joint filler, including the following components by weight: 65 parts of quartz sand, 20 parts of Portland cement, 8 parts of antioxidant, 2 parts of limestone, and 2 parts of silicone leveling agent , 2 parts of antifungal agent, 6 parts of inorganic aluminum salt water repellent.

[0015] The caulking agent disclosed in this embodiment has good water resistance, mildew and oxidation resistance, easy and safe construction, and is a good tile paving caulking agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a gap filler which comprises the following components in parts by weight: 30-70 parts of quartz sand, 20-30 parts of Portland cement, 3-10 parts of antioxidant, 1-3 parts of limestone, 1-3 parts of organosilicon leveling agent, 1-2 parts of mold preventive and 5-10 parts of inorganic aluminum salt waterproofing agent. The gap filler disclosed by the invention has the advantages of favorable water resistance, mold resistance and oxidation resistance, is easy and safe for construction, and thus, is a favorable gap filler for spreading and attaching ceramic tiles.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a caulking agent for laying ceramic tiles. Background technique [0002] The laying of ceramic tiles has become a common decoration in daily life. From home to hotels and other public places, from the ground to the wall, the decorative effect brought by ceramic tiles cannot be underestimated. However, in the process of laying and laying, bricks and bricks The joints between the blocks need to be specially treated. At present, the commonly used joint sealant is cement mortar, which has low adhesion and is prone to cracking after curing, thereby absorbing water. If it encounters thermal expansion and contraction, it will Cause the tiles to burst, or too much water seeps in and the adhesion between the tiles and the wall is not strong enough to fall off. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a caulking agent ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04
Inventor 田敬强
Owner QINGDAO BAOLIKANG NEW MATERIALS
PatSnap Eureka logo

PatSnap Eureka turns technology decisions into work you can execute. Powered by our Innovation Knowledge Graph, it runs expert workflows across engineering, life sciences, materials and intellectual property. Get your review-ready output in minutes.

X (Twitter)LinkedInYouTubeSubstack

© 2026 PatSnap. All rights reserved. 

Terms of Service

 | 

Privacy policy

 | 

Modern Slavery Act Transparency Statement