Barite anti-radiation pump concrete

A technology for pumping concrete and barite, applied in the field of barite anti-radiation pumping concrete, to achieve the effects of mechanized construction, simple structure and low price

Active Publication Date: 2014-05-21
SICHUAN HUASHI GREEN HOMELAND BUILDING MATERIALS
View PDF4 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the construction of the linear accelerator room, the traditional lead plate and other heavy metal materials are used as the shielding material, which is not only expensive, but also has a complicated structure.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Barite anti-radiation pump concrete
  • Barite anti-radiation pump concrete
  • Barite anti-radiation pump concrete

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A barite anti-radiation pumping concrete, the concrete is based on the component unit kg / m 3 The mixing ratio is: cement: water: barite powder: barite sand: barite: synergist: admixture = [340~450]: [110~170]: [75~150]: [1000~1400 ]: [1800~2000]: [2~4]: [7~19]. The apparent density of the obtained concrete is 3700-3850kg / m3, and the 28d compressive strength reaches 25-65MPa. It has good slump / expansion suitable for pumping and pouring, and has good resistance to gamma rays and neutron rays. shielding effect.

Embodiment 2

[0041] A kind of barite anti-radiation pumping concrete, said concrete is according to the component unit kg / m 3 The mixing ratio is: cement: water: barite powder: barite sand: barite: synergist: polycarboxylate additive = [340~400]: [140~163]: [85~100]: [1155~1345]: [1857~1957]: [2~4]: [7.6~14.6]. The apparent density of the obtained concrete is 3750-3800kg / m 3 , 28d compressive strength of 28-60MPa has a good slump / expansion suitable for pumping pouring, and has a good shielding effect on gamma rays and neutron rays.

Embodiment 3

[0043] A barite anti-radiation pumping concrete, the proportion of the concrete raw materials by weight is: 400 parts of cement, 140 parts of water, 100 parts of barite powder, 1155 parts of barite sand, 1988 parts of barite, synergistic 2.4 parts of agent, 14.6 parts of polycarboxylate additive. The available slump / expansion is 210mm / 495mm, and the apparent density is 3752kg / m 3 , 28d C50 grade radiation-resistant pumped concrete with a compressive strength of 59.7MPa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses barite anti-radiation pump concrete. The concrete comprises the following components: cement, water, barite powder, barite sand, barite, synergist and admixture according to a ratio of [340-450]:[110-170]:[75-150]:[1000-1400]:[1800-2000]:[2-4]:[7-19]. According to selection of raw materials and design of the ratio, the anti-radiation concrete which is high in density and high in liquidity and can be used for pumping is obtained.

Description

technical field [0001] The invention belongs to the technical field of concrete preparation and relates to a barite anti-radiation pumping concrete. Background technique [0002] Radiation-resistant concrete not only needs to meet the structural strength, but also needs to be heavy, contain more bound water, and have better homogeneity than ordinary concrete. No voids or cracks are allowed in the shrinkage of concrete during construction and service life. In the construction of the linear accelerator room, if the shielding body material is traditional heavy metal materials such as lead plates, it is not only expensive, but also has a complicated structure. [0003] In order to prevent the leakage of nuclear radiation from causing harm to the human body, a special radiation-resistant material is needed, and concrete with barite as the coarse and fine aggregate is one of them. In addition to absorbing X-rays and γ-rays, anti-radiation concrete must also have the ability to we...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B14/36
Inventor 刘登贤陈东吴鑫
Owner SICHUAN HUASHI GREEN HOMELAND BUILDING MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap