Gap filler

A technology of caulking agent and adhesive is applied in the field of caulking agent for tile paving, which can solve the problems of insufficient strength of the caulking agent, prone to cracking, tile bursting, etc., and achieves easy and safe construction, and promotes hydration. , the effect of increasing strength

Inactive Publication Date: 2014-05-21
QINGDAO BAOLIKANG NEW MATERIALS
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The laying of ceramic tiles has become a common decoration in daily life. From home to hotels and other public places, from the ground to the wall, the decorative effect brought by ceramic tiles cannot be underestimated. However, in the process of laying and laying, bricks and bricks The joints between the blocks need to be specially treated. At present, the commonly used joint sealant is cement mortar, which has low adhesion and is prone to cracking after curing, thus absorbing water. If it encounters thermal expansion and contraction, it will Cause the tiles to burst, or too much water seeps in and the adhesion between the tiles and the wall is not strong enough to fall off
Sometimes cellulose ether is added to the sealant to retain water, but the amount of cellulose ether added needs to be strictly controlled. If too much is added, it will be too viscous, and if too little is added, the water in the sealant will evaporate too quickly. The sealant is not strong enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] Example 1. This example discloses a caulking agent, including the following ingredients by weight: 48 parts of quartz sand, 25 parts of sulphoaluminate cement, 8 parts of antioxidants, 3 parts of adhesives, and 0.2 parts of cellulose ether. Parts, 1 part of anti-mold agent, 5 parts of inorganic aluminum salt water repellent agent, 8 parts of calcium carbonate.

Embodiment 2

[0010] Example 2. This example discloses a caulking agent, including the following ingredients by weight: 55 parts of quartz sand, 20 parts of sulphoaluminate cement, 5 parts of antioxidants, 2 parts of adhesives, and 0.5 parts of cellulose ether. Parts, 2 parts of anti-mold agent, 5 parts of inorganic aluminum salt water repellent, 10 parts of calcium carbonate.

Embodiment 3

[0011] Example 3, this example discloses a caulking agent, including the following ingredients by weight: 60 parts of quartz sand, 20 parts of sulphoaluminate cement, 3 parts of antioxidant, 1 part of adhesive, and 0.5 of cellulose ether. Parts, 2 parts of anti-mold agent, 5 parts of inorganic aluminum salt water repellent agent, 8 parts of calcium carbonate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a gap filler which comprises the following components in parts by weight: 40-70 parts of quartz sand, 8-12 parts of calcium carbonate, 20-30 parts of sulfoaluminate cement, 3-10 parts of antioxidant, 1-3 parts of adhesive, 0.2-0.6 part of cellulose ether, 1-3 parts of mold preventive and 5-10 parts of inorganic aluminum salt waterproofing agent. The quartz sand used as the main body component of the gap filler lowers the cost of the gap filler; the mold preventive is mainly used for preventing mold due to water absorption; the addition of the inorganic aluminum salt waterproofing agent can perform the waterproofing function after the gap filler is cured; and the sulfoaluminate cement can prevent the re-alkali phenomenon after use for some time, accelerate the hydration of cement and enhance the strength. The gap filler is easy and safe for construction, and thus, is a favorable gap filler for spreading and attaching ceramic tiles.

Description

Technical field [0001] The invention relates to the field of building materials, in particular to a joint sealant for tile paving. Background technique [0002] The paving of tiles has become a common decoration in daily life. From homes to hotels and other public places, from the ground to the wall, the decorative effect brought by the tiles cannot be underestimated. However, in the process of paving, bricks and bricks The caulking between blocks needs special treatment. At present, the commonly used caulking agent is cement mortar. This kind of caulking agent has low adhesion and is prone to cracking after curing, thereby absorbing moisture. If it encounters thermal expansion and contraction, it will Causes the tile to burst, or too much water infiltrates, causing the tile and the wall to not adhere firmly and fall off. Cellulose ether is sometimes added to the sealant to retain water, but the amount of cellulose ether added needs to be strictly controlled. Adding too much wil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/06C04B14/28C04B14/06
Inventor 田敬强
Owner QINGDAO BAOLIKANG NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products