A kind of fdy fiber with surface cracking and preparation method thereof

A fiber and speed technology, applied in the field of FDY fiber and its preparation, can solve problems such as insufficient

Active Publication Date: 2017-11-21
JIANGSU DELI CHEM FIBER CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This is only the use of the inherent properties of PBT itself to achieve the purpose of improving the performance of composite fibers, which is far from enough for the research on PBT-PET skin-core composite fibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A kind of preparation method of the FDY fiber of surface cracking, comprises the preparation method of low crystallization rate polyester and the preparation method of sheath-core composite fiber:

[0038] 1) The preparation method of the low crystallization rate polyester is divided into two steps of esterification reaction and polycondensation reaction:

[0039] Described esterification reaction:

[0040] Using terephthalic acid, ethylene glycol, isophthalic acid and 1,4-cyclohexanediol as raw materials, the molar ratio of terephthalic acid: ethylene glycol: isophthalic acid: 1,4-cyclohexanediol =100:120:0.5:0.5, make a homogeneous slurry and carry out the esterification reaction; the esterification reaction is carried out in a nitrogen atmosphere, the pressure is controlled at 0.4MPa, the temperature is controlled at 250°C, and the distilled amount of esterified water reaches the theoretical value 90% is the end point of the esterification reaction.

[0041] Descri...

Embodiment 2

[0048] A kind of preparation method of the FDY fiber of surface cracking, comprises the preparation method of low crystallization rate polyester and the preparation method of sheath-core composite fiber:

[0049] 1) The preparation method of the low crystallization rate polyester is divided into two steps of esterification reaction and polycondensation reaction:

[0050] Described esterification reaction:

[0051] Using terephthalic acid, ethylene glycol, isophthalic acid and 1,4-cyclohexanediol as raw materials, the molar ratio of terephthalic acid: ethylene glycol: isophthalic acid: 1,4-cyclohexanediol =100:120:1:2, make a uniform slurry and carry out the esterification reaction; the esterification reaction is pressurized in a nitrogen atmosphere, the pressure is controlled at 0.3MPa, the temperature is controlled at 245°C, and the amount of esterified water distilled reaches the theoretical 90% of the value is the end point of the esterification reaction.

[0052] Describ...

Embodiment 3

[0059] A kind of preparation method of the FDY fiber of surface cracking, comprises the preparation method of low crystallization rate polyester and the preparation method of sheath-core composite fiber:

[0060] 1) The preparation method of the low crystallization rate polyester is divided into two steps of esterification reaction and polycondensation reaction:

[0061] Described esterification reaction:

[0062] Using terephthalic acid, ethylene glycol, isophthalic acid and 1,4-cyclohexanediol as raw materials, the molar ratio of terephthalic acid: ethylene glycol: isophthalic acid: 1,4-cyclohexanediol =100:120:3:5, make a homogeneous slurry and carry out the esterification reaction; the esterification reaction is carried out in a nitrogen atmosphere, the pressure is controlled at 0.4MPa, the temperature is controlled at 230°C, and the distilled amount of esterified water reaches the theoretical value 90% is the end point of the esterification reaction.

[0063] Described ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
depthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a surface-cracked FDY fiber and a preparation method thereof. The surface-cracked FDY fiber is composed of a skin layer and a core layer, and has axial cracks on the surface. The material used for the skin layer is polyester with a high crystallization rate, and the material used for the core layer is polyester with a low crystallization rate. Due to the difference in the crystallization rate between the skin layer material and the core layer material, the cooling crystallization conditions of the skin layer and the core layer are different during the process of fiber ejection from the spinneret to cooling and stretching. The skin layer crystallizes quickly while the core layer is slower. When stretching, the cortex tends to produce axial cracks, and FDY fibers with surface cracks are obtained under orderly control.

Description

technical field [0001] The invention relates to a FDY fiber and a preparation method thereof, in particular to a surface-cracked FDY fiber and a preparation method thereof. Background technique [0002] Polyester (PET) is one of the most widely used synthetic polymers by humans. PET was synthesized as early as the 1940s, and it was found to have excellent properties, and it is widely used in textiles, packaging, and medical treatment. Sanitation, automobiles, electronic appliances, safety protection, environmental protection and other fields. With the progress of society and the improvement of people's living standards, the demand for the differentiation and functionalization of polyester fibers is getting higher and higher. The differentiated fibers of polyester are mainly characterized by form (fine denier, special-shaped cross-section, etc.), high performance (high strength, high modulus, low shrinkage, etc.), high function (high sensitivity, moisture absorption, moistur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More