High-strength wear-resistant tear-resistant rubber material

A rubber material, tear-resistant technology, applied in the field of rubber materials, to achieve the effect of improving heat resistance and flame retardancy, increasing strength and hardness, improving wear resistance and tear resistance

Active Publication Date: 2014-10-08
宁国日格美橡塑股份有限公司
View PDF3 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the carboxylated nitrile rubber material at this stage is still difficult to meet the use environment of mine mobile electrical equipment. Now it is necessary to improve the carboxylated nitrile rubber, continue to improve the wear resistance and tear resistance of the product, and make it suitable for mine mobile electrical equipment. surroundings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of high-strength abrasion-resistant and tear-resistant rubber material that the present invention proposes, its raw material comprises by weight:

[0016] 40 parts of carboxylated nitrile rubber, 30 parts of neoprene rubber, 10 parts of natural rubber, 20 parts of ethylene-octene copolymer, 5 parts of silane coupling agent, 2 parts of sulfur, 2 parts of magnesium oxide, 5 parts of zinc oxide, environmental protection 12.5 parts of flame retardant FR-T80, 2 parts of antimony trioxide, 20 parts of carbon microspheres, 15 parts of nano-carbon black, 20 parts of modified kaolin, 2 parts of CPE special stabilizer, 1.5 parts of stearic acid, diphenylene 7 parts of trioctyl triacid, 0.5 part of paraffin, wherein the modified kaolin is the kaolin whose surface is modified by fatty acid surfactant;

[0017] Carboxylated nitrile rubber, chloroprene rubber, natural rubber and ethylene-octene copolymer are blended and granulated; then continue to add silane coupling agent, m...

Embodiment 2

[0019] A kind of high-strength abrasion-resistant and tear-resistant rubber material that the present invention proposes, its raw material comprises by weight:

[0020] Carboxylated nitrile rubber 50 parts, neoprene rubber 20 parts, natural rubber 18 parts, ethylene-octene copolymer 12 parts, silane coupling agent 13 parts, sulfur 1.5 parts, magnesium oxide 4 parts, zinc oxide 2 parts, environmental protection 14 parts of flame retardant FR-T801, 1 part of antimony trioxide, 30 parts of carbon microspheres, 5 parts of nano-carbon black, 30 parts of modified kaolin, 1 part of CPE special stabilizer, 3 parts of stearic acid, trimellitic acid 5 parts of trioctyl esters, 1.5 parts of paraffin, wherein the modified kaolin is kaolin whose surface is modified by a silane coupling agent;

[0021] Carboxylated nitrile rubber, chloroprene rubber, natural rubber and ethylene-octene copolymer are blended and granulated; then continue to add silane coupling agent, magnesium oxide, zinc oxi...

Embodiment 3

[0023] A kind of high-strength abrasion-resistant and tear-resistant rubber material that the present invention proposes, its raw material comprises by weight:

[0024] Carboxylated nitrile rubber 45 parts, neoprene rubber 25 parts, natural rubber 15 parts, ethylene-octene copolymer 15 parts, silane coupling agent 10 parts, sulfur 1.8 parts, magnesium oxide 3 parts, zinc oxide 3 parts, environmental protection 13.6 parts of flame retardant FR-T80, 1.2 parts of antimony trioxide, 25 parts of carbon microspheres, 10 parts of nano-carbon black, 25 parts of modified kaolin, 1.8 parts of CPE special stabilizer, 2.7 parts of stearic acid, diphenylene 6 parts of trioctyl triate, 1 part of paraffin, wherein the modified kaolin is a modified kaolin whose surface is subjected to a zirconium coupling agent, and the particle size of the nano-carbon black is 50-80nm;

[0025] Carboxylated nitrile rubber, chloroprene rubber, natural rubber and ethylene-octene copolymer are blended and granu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-strength wear-resistant tear-resistant rubber material which is prepared from the following raw materials in parts by weight: 40-50 parts of carboxy nitrile rubber, 20-30 parts of chloroprene rubber, 10-18 parts of natural rubber, 12-20 parts of ethylene-octylene copolymer, 5-13 parts of silane coupling agent, 1.5-2 parts of sulfur, 2-4 parts of magnesium oxide, 2-5 parts of zinc oxide, 2.5-4 parts of environment-friendly flame retardant FR-T801, 1-2 parts of antimony trioxide, 20-30 parts of carbon microsphere, 5-15 parts of nano carbon black, 20-30 parts of modified kaolin, 1-2 parts of CPE special-type stabilizer, 1.5-3 parts of stearic acid, 5-7 parts of trioctyl trimellitate and 0.5-1.5 parts of paraffin. The rubber material has the advantages of excellent wear resistance, excellent tear resistance, high strength and high toughness.

Description

technical field [0001] The invention relates to the technical field of rubber materials, in particular to a high-strength, wear-resistant and tear-resistant rubber material. Background technique [0002] When wire and cable products are used in special occasions such as mine mobile electrical equipment or mining flexible cables on various mining machinery, they are subject to mechanical forces in the shearing direction, which requires wire and cable sheaths to have excellent wear resistance. Tear performance. The carboxylated nitrile rubber is made of ternary copolymerization of butadiene, acrylonitrile and organic acid, referred to as XNBR. The introduction of carboxyl groups into nitrile rubber can improve its tensile strength, tear strength, hardness, abrasion resistance, adhesion and ozone aging resistance, especially the tensile strength at high temperature. The introduction of carboxyl groups can also increase the polarity of the nitrile rubber molecule and increase ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L15/00C08L11/00C08L7/00C08L23/08C08K13/06C08K9/06C08K9/04C08K3/06C08K3/22C08K7/18C08K3/04C08K3/34C08K5/09C08K5/12C08K5/01
Inventor 李元焕
Owner 宁国日格美橡塑股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka