A kind of preparation method of polymer water-absorbing resin potassium phosphate water-retaining controlled-release fertilizer

A polymer water absorption, potassium phosphate technology, applied in fertilization equipment, fertilizer mixture, application, etc., can solve the problem of not having the function of water absorption and water retention

Active Publication Date: 2016-08-03
QINGDAO ZETIAN AGRI SCI & TECH CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current conventional fertilizers and slow-release and controlled-release fertilizers do not have the function of water absorption and water retention. In order to further promote the integrated interaction of fertilizer and water and improve the production efficiency of water and fertilizer, the water retention function of water-retaining agents, controlled release technology and fertilizer technology are combined. Among them, the research and development of water-retaining slow-release and controlled-release fertilizers is a practical production problem that needs to be solved urgently, and it is also a need for the theory and practice of water-fertilizer interaction and coupling.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A kind of preparation method of polymer water-absorbing resin potassium phosphate water-retaining controlled-release fertilizer of the present embodiment comprises the following contents:

[0025] (1) Prepare 1560g of 31.5% NaOH aqueous solution;

[0026] (2) Neutralization reaction: Continuously drop the prepared NaOH aqueous solution into 3000g of acrylic acid with a purity greater than 99.5% for neutralization reaction. The reaction time is 20 minutes. Add 1520g (phosphoric acid content ≥ 86%) phosphoric acid, 2200g ( Potassium oxide content ≥ 50%) potassium sulfate; then cool down to 56-65°C;

[0027] (3) Copolymerization reaction: Add 80g of polyethylene glycol crosslinking agent to the solution after neutralization reaction, stir at 90-100 rpm, add 15g of potassium persulfate initiator after 10 minutes, and heat to 65- The copolymerization reaction is carried out at 70°C, the temperature during the reaction is controlled at 110°C-115°C, and the reaction time is 1...

Embodiment 2

[0032] The preparation method of the polymer water-absorbing resin potassium phosphate water-retaining controlled-release fertilizer of the present embodiment includes the following contents:

[0033] (1) Prepare 1560g of 32.7% NaOH aqueous solution;

[0034] (2) Neutralization reaction: Continuously drop the prepared NaOH aqueous solution into 3000g of acrylic acid with a purity greater than 99.5% for neutralization reaction. The reaction time is 20 minutes. Add 1550g (phosphoric acid content ≥ 86%) phosphoric acid, 2160g ( Potassium oxide content ≥ 50%) potassium sulfate; then cool down to 56-65°C;

[0035] (3) Copolymerization reaction: Add 80g of polyethylene glycol crosslinking agent to the solution after neutralization reaction, stir at 90-100 rpm, add 15g of potassium persulfate initiator after 10 minutes, and heat to 65- The copolymerization reaction is carried out at 70°C, the temperature during the reaction is controlled at 110°C-115°C, and the reaction time is 15 min...

Embodiment 3

[0040] A kind of preparation method of polymer water-absorbing resin potassium phosphate water-retaining controlled-release fertilizer of the present embodiment comprises the following contents:

[0041] (1) Prepare 1560g of 31.9% NaOH aqueous solution;

[0042] (2) Neutralization reaction: Continuously drip the prepared NaOH aqueous solution into 3000g of acrylic acid with a purity greater than 99.5% for neutralization reaction. The reaction time is 20 minutes. Add 1570g (phosphoric acid content ≥ 86%) phosphoric acid, 2170g ( Potassium oxide content ≥ 50%) potassium sulfate; then cool down to 56-65°C;

[0043] (3) Copolymerization reaction: Add 80g of polyethylene glycol crosslinking agent to the solution after neutralization reaction, stir at 90-100 rpm, add 15g of potassium persulfate initiator after 10 minutes, and heat to 65- The copolymerization reaction is carried out at 70°C, the temperature during the reaction is controlled at 110°C-115°C, and the reaction time is 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
water absorptionaaaaaaaaaa
boiling pointaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of polymer water-absorbing resin potassium phosphate water-retaining controlled-release fertilizer, which comprises five steps of preparing sodium hydroxide aqueous solution, neutralization reaction, copolymerization reaction, solidification and drying, and pulverization, shortening the process flow and reducing production time ,reduce manufacturing cost. It solves the problem of damage to soil, water and air caused by a large number of traditional chemical fertilizers, and at the same time increases the content of phosphoric acid and potassium oxide elements in water-retaining and controlled-release fertilizers. There are no three wastes (waste, waste gas, waste water) in the production process, no pollution to the environment, safety and environmental protection, and stable product quality.

Description

technical field [0001] The invention relates to a preparation method of a polymer water-absorbing resin potassium phosphate water-retaining controlled-release fertilizer, specifically belonging to the production process of a polymer water-absorbing resin, also known as SAP. Background technique [0002] The preparation method of the present invention is a polymer water-absorbing resin potassium phosphate water-retaining controlled-release fertilizer, which is to bond the fertilizer nutrient group to the macromolecular skeleton structure through the production process of the polymer water-absorbing resin and the chemical modification method of the hydrophilic polymer On, so that it has both water absorption and water retention performance, and slow and controlled release performance. Potassium phosphate water-retaining and controlled-release fertilizer new material formed by polymerization of acrylic acid, sodium hydroxide, potassium sulfate, phosphoric acid, polyethylene gly...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F283/06C08F220/06C05G3/04C05G3/80
Inventor 朱彦芳
Owner QINGDAO ZETIAN AGRI SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com