A method for improving the emissivity of paint film

A technology of emissivity and paint film, applied in sputtering coating, vacuum evaporation coating, ion implantation coating and other directions, can solve the problem of high emissivity limitation and achieve the effect of high emissivity and good chemical stability

Active Publication Date: 2016-06-15
LANZHOU INST OF PHYSICS CHINESE ACADEMY OF SPACE TECH
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in some special occasions and special application conditions, it is not advisable to add fillers to increase emissivity. For example, in high temperature, strong ultraviolet radiation, space and other environments, the paint film needs to express information such as color and pattern. Such use conditions The color of the paint film is limited, which in turn limits the high emissivity coatings and fillers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for improving the emissivity of paint film
  • A method for improving the emissivity of paint film

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0029] According to the high emissivity paint film prepared by the above method, by such as figure 2 As shown, the paint film layer and the transparent emissivity adjustment film, wherein the material of the paint film layer is a silicone resin-based coating, the transparent emissivity adjustment film is a silicon dioxide film, and the thickness of the transparent emissivity adjustment film is 200nm.

example 2

[0031] The high-emissivity paint film prepared according to the above method is composed of a paint film layer and a transparent emissivity adjustment film, wherein the material of the paint film layer is a silicone resin-based coating, the transparent emissivity adjustment film is a silicon dioxide film, and the transparent emissivity adjustment The thickness of the film was 300 nm.

example 3

[0033] The high-emissivity paint film prepared according to the above method is composed of a paint film layer and a transparent emissivity adjustment film, wherein the material of the paint film layer is a silicone resin-based coating, the transparent emissivity adjustment film is a silicon dioxide film, and the transparent emissivity adjustment The thickness of the film was 300 nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A method for improving the emissivity of a paint film according to the present invention, the specific steps are: the first step, using an ion source to clean the paint film surface, and the cleaning time is controlled between 1min~10min; the second step, coating the paint film surface A transparent emissivity-adjusting thin film; the plating process is: using different sputtering rates to carry out sputtering deposition of a transparent emissivity-adjusting thin film on the surface of the paint film three times. The invention prepares a high-emissivity transparent thin film material on the surface of the paint film through a sputtering method so that the paint film has a high emissivity.

Description

technical field [0001] The invention relates to a method for increasing the emissivity of a paint film, which belongs to the technical field of thin films. Background technique [0002] Emissivity is used to characterize the ability of materials to radiate heat outward, and materials with high emissivity have a strong ability to radiate heat outward. High emissivity materials have important applications in satellite thermal control, energy saving and environmental protection. [0003] High-emissivity coating itself is a relatively mature product, and there are many related researches. Many types of coatings can also achieve the purpose of increasing emissivity by adding high-emissivity fillers. However, in some special occasions and special application conditions, it is not advisable to add fillers to increase emissivity. For example, in high temperature, strong ultraviolet radiation, space and other environments, the paint film needs to express information such as color an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C14/34C23C14/54C23C14/58C23C14/08C23C14/10C23C14/35
Inventor 李林许旻王洁冰赵印中吴春华左华平
Owner LANZHOU INST OF PHYSICS CHINESE ACADEMY OF SPACE TECH