Manufacturing method for ZnO nano tree array/polymer blend conformal structure hybrid solar cell
A technology of blending polymers and solar cells, which is applied in the field of solar cells, and can solve the problems that have not yet been seen in the application of hybrid solar cells to nano-tree arrays, and the height and density of nano-tree arrays are not suitable for polymer solar cells.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0018] The electrochemical deposition process was carried out in a 0.01 mol / L zinc nitrate aqueous solution. The power supply used was a two-electrode system with a constant voltage of 2.5 V, a constant temperature of 75 °C, and a deposition time of 20 min. The FTO glass substrate is connected to the cathode, and the anode is made of pure platinum, and the two electrodes are kept parallel with a distance of 2 cm. After the deposition was completed, all samples were washed repeatedly with deionized water to remove residual solution ions on the samples. Afterwards, the samples were placed in an air atmosphere heat treatment furnace for annealing at 150 °C. Subsequently, the sample was placed on an AALD (atmosphere atomic layer deposition) workbench at a temperature of 150 °C. The sample stage was placed 50 mm below the gas delivery pipe at 40 °C, and was repeatedly oscillated at a speed of 50 mm / s. Diethylzinc is used as the precursor of zinc, and pure water is used as the...
Embodiment 2
[0021] The electrochemical deposition process was carried out in a 0.05 mol / L zinc nitrate aqueous solution, the power supply used was a two-electrode system, the voltage was constant at 2 V, the temperature was constant at 95 °C, and the deposition time was 40 min. The FTO glass substrate is connected to the cathode, and the anode is made of pure platinum, and the two electrodes are kept parallel with a distance of 2 cm. After the deposition was completed, all samples were washed repeatedly with deionized water to remove residual solution ions on the samples. Afterwards, the samples were placed in an air atmosphere heat treatment furnace for annealing at 150 °C. Subsequently, the sample was placed on the AALD workbench at a temperature of 150 °C, and the sample stage was placed 50 mm below the gas pipeline at 40 °C, and the vibration movement was repeated at a speed of 20 mm / s. Diethylzinc is used as the precursor of zinc, and pure water is used as the oxidant. Nitroge...
PUM
Property | Measurement | Unit |
---|---|---|
Height | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap