Steel structure surface insulation and anti-corrosion coating

A technology for anti-corrosion coatings and steel structures, applied in the direction of anti-corrosion coatings, coatings, etc., can solve the problems of large influence of seasons and climates, failure to achieve thermal insulation effect, low bond strength of substrates, etc., to increase equipment load, light weight, and use long life effect

Active Publication Date: 2016-11-23
SHENZHEN HUACHUANG CHEM
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the traditional thermal insulation technology is mainly rock wool technology. The main disadvantage of rock wool technology is that it is highly corrosive, and it is easy to corrode the steel structure of containers, equipment or pipelines. Rock wool cannot see water, otherwise it will greatly affect the thermal insulation effect; traditional Insulation technology also includes composite silicate technology. The main disadvantage of silicate insulation materials is that the drying cycle is long, the construction is greatly affected by seasons and climates, and the bonding strength to the substrate is low. Improper construction can easily cause large-scale hollowing.
The above-mentioned traditional thermal insulation technologies cannot achieve the ideal thermal insulation effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Weigh excipients: 3g dispersant P-19, 3g wetting and dispersing agent W-18, 8g deionized water, 8g CPA-100P airgel particles, 2g stabilizer Aliso™RM-825; Weigh main ingredients: 9g Special ceramic particles, 6g rutile titanium dioxide R258, 10g F-197# bisphenol A type anticorrosion resin, 13g vinyl ester resin, 13g silicone-acrylic resin ACR-901, 6g nano-rare earth, 3g special flame retardant SF- 018; Weigh additives: 2g silicone defoamer, 1g fluorocarbon modified polyacrylate leveling agent, 1g polyacrylate thickener, 1g water-based epoxy resin curing agent, 2g dipropylene glycol methyl ether, 3g dipropylene glycol Butyl ether, 6g deionized water.

[0025] The preparation process of the steel structure surface thermal insulation and anticorrosion coating is as follows:

[0026] 1) Put 3% dispersant P-19, 3% wetting and dispersing agent W-18, and 6% deionized water into a beaker according to the ratio of 1:1:2, and disperse homogeneously on a high-speed disperser for a...

Embodiment 2

[0030] Weigh auxiliary materials: 4g dispersant P-19, 4g wetting and dispersing agent W-18, 9g deionized water, 7g CPA-100P airgel particles, 1g stabilizer Aliso™ RM-825; Weigh main ingredients: 8g Special ceramic particles, 7g rutile titanium dioxide R258, 11g F-197# bisphenol A type anticorrosion resin, 12g vinyl ester resin, 12g silicone-acrylic resin ACR-901, 7g nano-rare earth, 3g special flame retardant SF- 018; Weigh additives: 2g silicone defoamer, 1g fluorocarbon modified polyacrylate leveling agent, 2g polyacrylate thickener, 1g water-based epoxy resin curing agent, 2g dipropylene glycol methyl ether, 2g dipropylene glycol Butyl ether, 6g deionized water.

[0031] The preparation process of the steel structure surface thermal insulation and anticorrosion coating is as follows:

[0032]1) According to the ratio of 1:1:2, put 4% dispersant P-19, 4% wetting and dispersing agent W-18, and 8% deionized water into a beaker and disperse homogeneously on a high-speed disper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a steel structure surface insulation anticorrosion paint. The steel structure surface insulation anticorrosion paint comprises the following components by weight percentage: a main material is composed of 5-9% of special ceramics particles, 5-7% of rutile titanium dioxide R258, 10-12% of F-197# bisphenol A anticorrosion resin, 12-15% of vinyl ester resin, 10-14% of organosilicon-acrylic resin ACR-901, 6-8% of nano rare earth and 2-3% of special fire retardant; and an auxiliary material composed of 6-9% of CPA-100P aerogel particles, 2-4% of dispersant P-19, 2-4% of wetting dispersant W-18, 1-2% of stabilizing agent Acrysol<TM> RM-825, 5-10% of deionized water; and 20% of additive. The insulation anticorrosion paint has the advantages of low conductivity, good insulation effect, anticorrosion and moisture resistance.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a thermal insulation and anticorrosion coating for the surface of steel structures. Background technique [0002] The steel structure surface of industrial containers and equipment is suitable for the outer surface of petroleum, petrochemical, electric power, railway, food, electronics and other related equipment. Insulation treatment is very critical when the temperature is high in summer. At present, the traditional thermal insulation technology is mainly rock wool technology. The main disadvantage of rock wool technology is that it is highly corrosive, and it is easy to corrode the steel structure of containers, equipment or pipelines. Rock wool cannot see water, otherwise it will greatly affect the thermal insulation effect; traditional Insulation technology also includes composite silicate technology. The main disadvantage of silicate insulation materials is that the drying cycle is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D5/08C09D201/02
CPCC08K2201/011C08L2205/035C09D5/08C09D7/61C09D133/04C09D201/00C08L101/00C08L33/02C08L33/04
Inventor 张毅
Owner SHENZHEN HUACHUANG CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com