A kind of preparation method of bamboo charcoal fiber fabric for home textile

A bamboo charcoal fiber and fabric technology, which is applied in the processing of textile materials, continuous processing of textile materials, fiber processing and other directions, can solve the problems of softness and antibacterial properties of fiber materials that need to be improved, and achieve stable jacquard quality, good hand feeling, high-end effect

CN104294402BActive Publication Date: 2016-02-17江苏宜妆生物科技有限公司
5 Cites 0 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Patents(China)
Current Assignee / Owner
Publication Date
2016-02-17

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention relates to a preparation method of textiles, in particular to a preparation method of bamboo charcoal fiber fabrics for home textiles, which comprises preparation of bamboo charcoal micropowder emulsion: adding a dispersant and bamboo charcoal micropowder in deionized water, and stirring to obtain a uniformly dispersed bamboo charcoal micropowder emulsion; The concentration of described bamboo charcoal micropowder is 50-80g / L; The weight ratio of dispersant and described bamboo charcoal micropowder is 6-9:100; Viscose liquid preparation; Bamboo charcoal fiber thread preparation: viscose liquid and described bamboo charcoal micropowder emulsion Mix evenly according to the weight ratio of 100:20-30, and then send to the spinning machine to make bamboo charcoal fiber filaments; gray fabric preparation: including spinning, warping, sizing, weaving, fabric post-treatment, opening, dehydration, drying and sewing steps ; In the spinning, cotton fiber is used in the warp direction, and modal fiber or spandex covering silk and the bamboo charcoal fiber silk are used in the weft direction; , Making overprinted flower screens. The bamboo charcoal fiber fabric for home textile prepared by the method has good softness and antibacterial property.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to a preparation method of textiles, in particular to a preparation method of bamboo charcoal fiber fabrics for home textiles. Background technique

[0002] Bamboo charcoal has good deodorizing, anti-corrosion, and odor-absorbing functions. Nano-scale bamboo charcoal powder also has antibacterial and bactericidal effects, as well as far-infrared and negative ion properties. CN103556263A (2014-2-5) discloses a hollow bamboo charcoal viscose fiber and its production process, but the softness and bacteriostasis of the fiber material prepared by this method still need to be improved. Contents of the invention

[0003] The purpose of this invention is to provide a kind of preparation method of softness and good bacteriostasis bamboo charcoal fiber fabric for home textile.

[0004] Above-mentioned technical purpose of the present invention is achieved through the following technical solutions:

[0005] A kind of preparation method ...

Examples

Embodiment 1

[0047] Preparation of nano silver:

[0048] A. Add sodium dodecylsulfonate solution, water-based polyacrylate and hydrazine hydrate solution to silver nitrate aqueous solution to obtain a mixed solution, the molar ratio of sodium dodecylsulfonate to silver nitrate is 4:1; The molar ratio of acrylate to silver nitrate is 0.4:1; the molar ratio of hydrazine hydrate to silver nitrate is 0.2:1;

[0049] B. Add dicyclohexyl-18-crown-6 and sodium metaphosphate to the mixture, the molar ratio of dicyclohexyl-18-crown-6 to silver nitrate is 3:1; sodium metaphosphate and nitric acid The molar ratio of silver is 0.8:1, and the pH value is controlled to be 8-9 to obtain nano silver.

[0050] The composition ratio of the viscose liquid used for bamboo charcoal fiber fabrics:

[0051] 25 parts of phthalic anhydride, 7 parts of furfuryl alcohol extracted from corncob residue, 10 parts of triethylene glycol, 15 parts of glutaric acid, 8 parts of butanetriol, 5 parts of zinc oxide powder, 3...

Embodiment 2

[0074] Preparation of nano silver:

[0075] A. Add sodium dodecylsulfonate solution, water-based polyacrylate and hydrazine hydrate solution to silver nitrate aqueous solution to obtain a mixed solution, the molar ratio of sodium dodecylsulfonate to silver nitrate is 6:1; The molar ratio of acrylate to silver nitrate is 0.6:1; the molar ratio of hydrazine hydrate to silver nitrate is 0.3:1;

[0076] B. Add dicyclohexyl-18-crown-6 and sodium metaphosphate to the mixture, the molar ratio of dicyclohexyl-18-crown-6 to silver nitrate is 5:1; sodium metaphosphate and nitric acid The molar ratio of silver is 1.3:1, and the pH value is controlled to be 8-9 to obtain nano silver.

[0077] The composition ratio of the viscose liquid used for bamboo charcoal fiber fabrics:

[0078] 35 parts of phthalic anhydride, 11 parts of furfuryl alcohol extracted from oat or wheat bran, 12 parts of triethylene glycol, 18 parts of glutaric acid, 10 parts of butanetriol, 7 parts of zinc oxide powde...

Embodiment 3

[0100] Preparation of nano silver:

[0101] A. Add sodium dodecylsulfonate solution, water-based polyacrylate and hydrazine hydrate solution to silver nitrate aqueous solution to obtain a mixed solution, the molar ratio of sodium dodecylsulfonate to silver nitrate is 5:1; The molar ratio of acrylate to silver nitrate is 0.5:1; the molar ratio of hydrazine hydrate to silver nitrate is 0.25:1;

[0102] B. Add dicyclohexyl-18-crown-6 and sodium metaphosphate to the mixture, the molar ratio of dicyclohexyl-18-crown-6 to silver nitrate is 4:1; sodium metaphosphate and nitric acid The molar ratio of silver is 1:1, and the pH value is controlled to be 8-9 to obtain nano silver.

[0103] The composition ratio of the viscose liquid used for bamboo charcoal fiber fabrics:

[0104] 30 parts of phthalic anhydride, 7-11 parts of furfuryl alcohol extracted from bamboo sawdust, 11 parts of triethylene glycol, 16 parts of glutaric acid, 9 parts of butanetriol, 6 parts of zinc oxide powder, ...