One-step production method of chlorinated polyethylene

A technology for chlorinated polyethylene and high-density polyethylene, which is applied in the field of one-step production of chlorinated polyethylene and its preparation, can solve the problems of producing chlorinated polyethylene without a one-step method, and can reduce production costs and save water resources. , The effect of reducing floor space and equipment investment

Active Publication Date: 2015-02-04
ANHUI RES INST OF CHEM IND
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Whether it is a patent or various documents, there is no report on the production of chlorinated polyethylene in one step

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • One-step production method of chlorinated polyethylene

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Dissolve 2.0g of sodium dodecylbenzenesulfonate, 8.0g of OP-10, 10.0g of polyolefin pyrrolidone (k-30), and 70.0g of active silicon dioxide in 1000g of water, put them into the reactor, and add 1.0g benzoyl peroxide, 100.0g high-density polyethylene, seal the reactor, raise the temperature to 80°C, start to feed chlorine gas, when the temperature rises to 135°C, feed 110.0g chlorine gas in total, stop chlorine flow The time is 2.5 hours, and the reaction is kept at 135° C. for 1 hour. Calcium oxide is added in batches during the reaction process, the calcium oxide is added at a rate such that the pH value of the reaction system is controlled between 7.0 and 8.5, and the total amount of calcium oxide added is 40 g.

[0025] When the kettle temperature drops to 80°C, the reaction system is purged with compressed air, the materials in the kettle are centrifuged, and the solid chlorinated polyethylene is dried to obtain a CPE product with a chlorine content of 35.5%; the ce...

Embodiment 2

[0027] Dissolve 0.3g sodium dodecylbenzenesulfonate, 0.7g OP-10, and 5.0g polyolefin pyrrolidone (k-30) in 1000g water, put them into the reactor, and add 5.0g of benzoyl peroxide to the reactor in turn , 200.0g high-density polyethylene airtight reactor, heat up to 80°C, start to feed chlorine gas, when the temperature rises to 135°C, feed 210.0g of chlorine gas in total, stop chlorine flow, chlorine flow time is 2.5 hours, keep warm at 135°C 1 hour. Calcium oxide was added in batches during the reaction, the rate of calcium oxide addition was such that the pH value of the reaction system was controlled between 7.0 and 8.5, and the total amount of calcium oxide added was 81 g.

[0028] When the temperature of the kettle drops to 80°C, the reaction system is purged with compressed air, the materials in the kettle are centrifuged, and the solid chlorinated polyethylene is dried to obtain a CPE product with a chlorine content of 36.0%; the centrifuged mother liquor is concentrat...

Embodiment 3

[0030] Dissolve 2.0g of sodium dodecylbenzenesulfonate, 8.0g of OP-10, 10.0g of polyolefin pyrrolidone (k-30), and 70.0g of active silica in 1000g of water, put them into the reactor, and add 1.0 g azobisisobutyronitrile, 100.0g high-density polyethylene, seal the reactor, raise the temperature to 80°C, and start to feed chlorine gas. The time is 2.5 hours, and the temperature is kept at 135° C. for 1 hour. Calcium oxide is added in batches during the reaction process, the calcium oxide is added at a rate such that the pH value of the reaction system is controlled between 7.0 and 8.5, and the total amount of calcium oxide added is 40 g.

[0031] When the kettle temperature drops to 80°C, the reaction system is purged with compressed air, the materials in the kettle are centrifuged, and the solid chlorinated polyethylene is dried to obtain a finished product with a chlorine content of 35.8% CPE; the centrifuged mother liquor is concentrated and dried to obtain a dihydrate with ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a one-step production method of chlorinated polyethylene. The method comprises the following steps: adding 10-20 parts by mass of high-density polyethylene to 80-90 parts by mass of water to generate a chlorination in the presence of an emulgator, a dispersing agent, an initiator and chlorine gas, adding 5-7 parts by mass of calcium oxide in batches in the chlorination process, thus generating chlorinated polyethylene resin and an aqueous solution of calcium chloride, wherein the addition speed of calcium oxide has to ensure that the pH value of the reaction system is controlled to be between 7.0 and 8.5; centrifuging and drying the obtained chlorinated polyethylene resin to obtain a finished chlorinated polyethylene product; and concentrating and drying the aqueous solution of calcium chloride to obtain a byproduct calcium chloride. The one-step production method of chlorinated polyethylene has the advantages that the process flow is simplified, the space occupied by devices and investment in devices are reduced, and the production cost is lowered; in the preparation process of chlorinated polyethylene, waste acid water is made a full use and prepared into a byproduct, and therefore the clean production level is high and relatively high economic benefit can be created.

Description

1. Technical field [0001] The present invention relates to the preparation method of macromolecular compound, exactly one-step method production chlorinated polyethylene and its preparation method. 2. Background technology [0002] At present, the industrialized chlorinated polyethylene (CPE) production equipment that has been built in my country generally adopts the water phase production process, that is, the polyethylene (PE) powder is dispersed in the water phase medium and chlorine gas is introduced, and the chlorinated modified polyethylene is produced. Get CPE products. The reaction process is as follows: [0003] [0004] It can be seen from the above reaction principle that in the production process of the water phase method, hydrogen chloride products are generated, and hydrochloric acid is formed in the water phase system, and the generated CPE is a porous elastic polymer material, resulting in a large amount of hydrochloric acid adsorbed on the surface and int...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F110/02C08F8/22
Inventor 何勇陈蔚林蒋苗梁琳唐勇孔祥杰何海辉刘晖刘立进
Owner ANHUI RES INST OF CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com