A kind of polyurethane foam, its preparation method and its application

A polyurethane foam and foam stabilizer technology, applied in the field of superhydrophobic polyurethane foam, polyurethane foam, and its preparation, can solve the problems of poor hydrophobic performance, achieve high hydrophobicity, low surface energy, and avoid secondary water removal problems

Active Publication Date: 2017-03-15
SOUTHWEAT UNIV OF SCI & TECH +3
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a kind of polyurethane foam, its preparation method and its application in view of the poor hydrophobic performance of the existing polyurethane foam.
The invention can effectively overcome the defect of poor hydrophobic performance of the existing polyurethane foam, and the polyurethane foam provided has superhydrophobic characteristics, and can selectively absorb oil and liquid organic pollutants for liquid organic pollutants and oil products leaked to the water surface And can not absorb water at all, so as to achieve the purpose of oil-water separation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polyurethane foam, its preparation method and its application
  • A kind of polyurethane foam, its preparation method and its application
  • A kind of polyurethane foam, its preparation method and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0065] The superhydrophobic polyurethane foam in this embodiment weighs each raw material component according to the following mass ratio: 25kg isocyanate, 35kg hydroxyl-terminated liquid rubber, 2kg catalyst, 0.5kg foam stabilizer, 2kg blowing agent, 3kg cell opener, 15kg resistance Fuel. Among them, the isocyanate in this embodiment is polymethylene polyphenyl polyisocyanate, the hydroxyl-terminated liquid rubber is grafted with aliphatic amine to epoxidize hydroxyl-terminated polybutadiene, and the catalyst is a combination of tertiary ammonia catalyst and organometallic catalyst. catalyst.

Embodiment 2

[0067] The superhydrophobic polyurethane foam in this embodiment includes the following components: 25kg isocyanate, 40kg hydroxyl-terminated liquid rubber, 2kg catalyst, 0.7kg foam stabilizer, 3kg blowing agent, 3kg cell opener, 10kg flame retardant. The isocyanate in this embodiment is polymethylene polyphenyl polyisocyanate; the carboxyl-terminated liquid rubber is aliphatic amine grafted carboxyl-terminated polybutadiene acrylonitrile; the catalyst is a composite catalyst of a tertiary ammonia catalyst or an organometallic catalyst.

Embodiment 3

[0069] (1) Preparation of aliphatic amine grafted hydroxyl-terminated polybutadiene acrylonitrile

[0070] Add octadecylamine and carboxyl-terminated polybutadiene acrylonitrile (number-average molecular weight 2000, nitrile group content 15%) in the reactor, wherein the nitrile functional group of carboxyl-terminated polybutadiene acrylonitrile and the amino functional group of octadecylamine The molar ratio is 1:1.3. Then add chloroform into the reactor, ultrasonically mix for 15 minutes, react at 65° C. for 4 hours, test the group change by infrared, and the reaction ends when the characteristic peak of the nitrile group disappears. The product obtained from the reaction was submerged in an alcoholic solvent to precipitate naturally, and then distilled under reduced pressure at 95°C and a pressure of -0.95MPa for 3 hours to obtain polybutadiene acrylonitrile grafted with aliphatic amines.

[0071] (2) Preparation of aliphatic amine grafted epoxidized hydroxyl-terminated po...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses polyurethane foam and a preparation method and application thereof, and the purpose is to solve the problems of poor hydrophobic performance of the existing polyurethane foam. The polyurethane foam includes isocyanate, hydroxyl terminated liquid rubber, a catalyst, a foaming agent, a foam stabilizer, a hole opening agent, a flame retardant, fatty amine and the like. Through use of low surface energy and high hydrophobic performance of the fatty amine and reaction performance of nitrile group (-CN) and epoxy group (-CH (O) CH-), the fatty amine is introduced into the nitrile group or epoxy group-containing hydroxyl terminated liquid rubber and nitrile group or epoxy group-containing carboxyl terminated liquid rubber, and by reaction with the isocyanate, the super hydrophobic polyurethane foam is prepared. When the super hydrophobic polyurethane foam absorbs oil-water mixtures, or oil and liquid organic matters leaking onto the water surface, only oil and liquid organic matters are absorbed, no water is absorbed, so that recovery of leaked oil and liquid organic matters and water purification can be realized.

Description

technical field [0001] The invention relates to the field of polymer materials, in particular to a polyurethane foam, its preparation method and its application. Specifically, the present invention relates to a superhydrophobic polyurethane foam, its preparation method and its application. Background technique [0002] Polyurethane foam is a kind of polymer foam material produced by polyaddition reaction between isocyanate monomer and compounds containing active hydrogen (such as -OH, -COOH, -NH-, etc.) in the presence of foaming agent. . Its main features are: porosity and low relative density. At the same time, it also has excellent physical and mechanical properties, acoustic properties, electrical properties and chemical resistance, and is widely used in home furnishing, transportation, construction industry, packaging materials and military aerospace industry and other fields. [0003] At present, the application of polyurethane foam to the treatment of typical toxic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L75/14C08K13/04C08K7/24C08K3/04C08K3/32C08K5/3492C08J9/14C08G18/76C08G18/69C08G59/50C08G69/34C09K3/32
Inventor 刘海东应琴贾飞
Owner SOUTHWEAT UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com