Method for manufacturing arc welded structural members

一种电弧焊接、结构构件的技术，应用在电弧焊设备、焊接介质、制造工具等方向，能够解决强度、疲劳特性降低、耐腐蚀性降低等问题，达到自由度大、优异耐熔融金属脆化裂纹性的效果

Inactive Publication Date: 2016-11-09
NISSHIN STEEL CO LTD
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If molten metal embrittlement cracks occur, this becomes the base point of corrosion and the corrosion resistance decreases
In addition, there are cases where strength and fatigue characteristics are lowered and become a problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for manufacturing arc welded structural members
  • Method for manufacturing arc welded structural members
  • Method for manufacturing arc welded structural members

Examples

Experimental program
Comparison scheme
Effect test

experiment example 1

[0067] The molten Zn-Al-Mg-based plated steel sheet shown in Table 1 was placed horizontally, and a weld bead (build-up welding) was formed on the surface of the steel sheet by an arc generated from a horizontally moving torch. The welding conditions are described in Table 1. For the section perpendicular to the direction of the weld bead including the weld seam and its nearby base metal, after mirror grinding and corrosion with nitric acid ethanol corrosion solution with a concentration of 0.2 volume % nitric acid, a scanning electron microscope is used to observe the weld bead seam. Near the edge, measure Figure 5 The length of the coating evaporation area shown by the symbol L in the middle.

[0068] [Table 1]

[0069]

[0070] Figure 6 Indicates its result. Figure 6 The case where the length of the plating evaporation region is 0.3 mm or more is drawn with the ○ mark, and the case of less than 0.3 mm is drawn with the X mark. With welding input heat Q(J / cm) and ...

experiment example 2

[0072] The molten Zn-Al-Mg system plated steel sheet shown in Table 1-2 (the plate thickness of the plated plate is 2.6 mm) is placed horizontally, and a weld bead is formed on the surface of the steel plate by an arc generated from a horizontally moving welding torch (surfacing welding ( Bird On Plate)). Welding conditions are recorded in Table 1-2. By observing the vicinity of the edge of the weld bead with the same method as in the above-mentioned experimental example 1, it is determined that Figure 5 The length of the coating evaporation area shown by the symbol L in the middle.

[0073] [Table 1-2]

[0074]

[0075] Figure 8 Indicates its result. Figure 8 The case where the length of the plating evaporation region is 0.3 mm or more is drawn with the ○ mark, and the case of less than 0.3 mm is drawn with the X mark. With welding input heat Q(J / cm) and CO in shielding gas 2 Concentration C CO2 (volume%) is related to C CO2 =205Q -0.32 The curve of is the boun...

Embodiment 1

[0090]A cold-rolled steel strip with a thickness of 3.2 mm and a width of 1000 mm having the composition shown in Table 2 was used as a coating original plate, and passed through a molten coating line to produce molten Zn-Al-Mg systems with various coating compositions. Plated steel. Each molten Zn-Al-Mg-based plated steel sheet was subjected to gas-shielded arc welding according to the test method shown below, and the influence of the shielding gas composition on the resistance to molten metal embrittlement cracking was investigated. The composition of the plating layer, the amount of plating deposition, and the composition of the shielding gas are shown in Table 4 below. The composition of the protective gas applied to the example of the present invention contains CO 2 : 0 to 16% by volume, remainder: one or more of Ar and He (the same applies to Examples 2 and 3 described later).

[0091] [Table 2]

[0092]

[0093] (Test method for resistance to molten metal embrittl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The present invention provides an arc-welded structural member using a Zn-Al-Mg-based plated steel plate member that has excellent resistance to molten metal embrittlement cracking without the restriction of the steel type of the plated original plate and a significant increase in cost Method of manufacturing arc welded structural members. Wherein, when steel materials are joined to each other by gas-shielded arc welding to manufacture welded structural members, at least one member to be joined is a molten Zn-Al-Mg-based plated steel member, and Ar gas, He gas, or Ar gas is used as a shielding gas. A gas adjusted so that the CO2 concentration CCO2 (volume %) satisfies the following formula (2) according to the welding heat input Q (J / cm) based on the +He mixed gas. 0≤CCO2≤2900Q-0.68...(2).

Description

technical field [0001] The present invention relates to a method of manufacturing an arc welded structural member excellent in resistance to molten metal embrittlement cracking, which is formed by using a molten Zn-Al-Mg plated steel sheet member for one or both members to be joined. Background technique [0002] Since the hot-dip zinc-based plated steel sheet is excellent in corrosion resistance, it is used in a wide range of applications including building components and automotive components. In particular, molten Zn—Al—Mg-based plated steel sheets maintain excellent corrosion resistance over a long period of time, and therefore demand has increased as a material to replace conventional molten zinc-plated steel sheets. [0003] The coating of the molten Zn-Al-Mg plated steel sheet is as described in Patent Documents 1 and 2, and has a ratio of Zn / Al / Zn 2 In the matrix of the Mg ternary eutectic, the primary crystal Al phase or the metal phase of the primary crystal Al ph...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K9/23B23K9/16B23K9/173C22C18/04C22C38/14C22C38/00
CPCB23K9/173B23K9/23B23K35/004B23K35/38B23K35/383B32B15/013C22C18/00C22C18/04C22C38/02C22C38/04C22C38/06C22C38/12C22C38/14B23K9/235C23C2/06
Inventor 细见和昭延时智和朝田博
Owner NISSHIN STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com