Production technology of art porcelain with rice paper painting effect

A production process and artistic technology, which is applied in the production process field of rice paper painting effect art porcelain, can solve the problems affecting the yield and work efficiency, the deformation of the green body, bumping and other problems, and achieve high strength, low cost, and avoid the effect of bumping and damage

Active Publication Date: 2017-08-11
SHANDONG GUIYUAN ADVANCED CERAMICS
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this process is a one-time firing process, which may cause bumps during the painting process. At the same time, after the firing is completed, there may be problems such as body deformation and air bubbles, which will affect the yield and work efficiency.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The production technology of described rice paper painting effect artistic porcelain, comprises the following steps:

[0023] (1) apply a layer of rice paper glaze on the surface of the porcelain biscuit;

[0024] The chemical weight percentage of described alkene art porcelain biscuit is composed of: SiO 2 67.62%, Al 2 o 3 24.14%, K 2 O5.2%, Na 2 O 1.34%, Li 2 O 0.44%, CaO 0.2%, MgO 0.46%, impurities 0.6%;

[0025] The chemical weight percent of described rice paper glaze is composed of: SiO 2 60.6%, Al 2 o 3 10.08%, B 2 o 3 4.41%, KNaO 3.77%, ZnO 7.81%, CaO 11.73%, MgO 1.6%;

[0026] (2) After the glazed surface is dry, the glazed enamel art porcelain biscuit is fired at 800°C at a low temperature, and the holding time is 15 minutes;

[0027] (3) drawing patterns on the glazed surface after low-temperature firing;

[0028] (4) Glaze-fire the semi-finished product after the pattern is drawn, the firing temperature is 1160°C, and the temperature is kept for...

Embodiment 2

[0031] The production technology of described rice paper painting effect artistic porcelain, comprises the following steps:

[0032] (1) apply a layer of rice paper glaze on the surface of the porcelain biscuit;

[0033] The chemical weight percentage of described alkene art porcelain biscuit is composed of: SiO 2 68.196%, Al 2 o 3 22.254%, K 2 O4.83%, Na 2 O 1.97%, Li 2 O 0.46%, CaO 0.9%, MgO 0.99%, impurity 0.4%;

[0034] The chemical weight percent of described rice paper glaze is composed of: SiO 2 60.17%, Al 2 o 3 11.00%, B 2 o 3 4.26%, KNaO3.64%, ZnO 7.52%, CaO 11.31%, MgO 2.10%;

[0035] (2) After the glazed surface is dry, fire the glazed enamel art porcelain biscuit at 820°C at a low temperature for 15 minutes;

[0036] (3) drawing patterns on the glazed surface after low-temperature firing;

[0037] (4) Glaze-fire the semi-finished product after pattern drawing, at a firing temperature of 1180° C., and keep it warm for 15 minutes.

Embodiment 3

[0039] The production technology of described rice paper painting effect artistic porcelain, comprises the following steps:

[0040] (1) apply a layer of rice paper glaze on the surface of the porcelain biscuit;

[0041] The chemical weight percentage of described alkene art porcelain biscuit is composed of: SiO 2 70.597%, Al 2 o 3 22.763%, K 2 O4.29%, Na 2 O 1.19%, Li 2 O 0.5%, CaO 0.2%, MgO 0.26%, impurities 0.2%;

[0042] The chemical weight percent of described rice paper glaze is composed of: SiO 2 67.95%, Al 2 o 3 9.72%, B 2 o 3 3.19%, KNaO2.58%, ZnO 4.37%, CaO 11.09%, MgO 1.1%;

[0043] (2) After the glazed surface is dry, fire the glazed enamel art porcelain biscuit at 850°C at a low temperature, and the holding time is 20 minutes;

[0044] (3) drawing patterns on the glazed surface after low-temperature firing;

[0045] (4) Glaze-fire the semi-finished product after the pattern is drawn, the firing temperature is 1200°C, and the temperature is kept for 15...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a production process of rice paper painting effect art porcelain, which belongs to the technical field of art porcelain production. The production process of the rice paper painting effect art porcelain of the present invention comprises the following steps: (1) applying one layer of rice paper glaze on the surface of the biscuit body of the associating art porcelain; The porcelain biscuit is fired at a low temperature; (3) the pattern is drawn on the glaze surface after the low temperature firing; (4) the semi-finished product after the pattern is drawn is glaze fired. The invention has the advantages of simple operation and low cost, and the prepared art porcelain has bright glaze surface, full color, no lead and cadmium dissolution, and has the painting effect of rice paper.

Description

technical field [0001] The invention relates to a production process of rice paper painting effect art porcelain, which belongs to the technical field of art porcelain production. Background technique [0002] With the progress of society and the continuous improvement of living standards, people's demand for ceramics has begun to move closer to the direction of practicality and artistry. Now the common decoration methods of art porcelain in the market are decals and overglaze painting. The product picture is easy to wear and tear, and will dissolve lead, cadmium and other elements that have an impact on human health. [0003] At present, CN101613204B discloses a production process of in-glaze bone china, which is to hang a layer of mixed glaze on the surface of the bone china blue body, draw after biscuit firing at 650-800°C, and then sinter at a high temperature of 1200-1245°C. Finished after firing, polishing and glaze firing. However, this process is a one-time firing ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B44C5/04C04B35/14C04B41/86
Inventor 张金钊桑爱美岳剑单婷任允鹏